Method of making a composite material including a thermoplastic polymer, a pest food material and a pesticide
View Patent ↗Composite materials that are palatable to a wood-destroying pest species and also pesticidal to the pest species can be used in pest control devices and can be used as wood substitutes for structural components, which are resistant to destruction by wood-destroying pests. The composite materials include a thermoplastic polymer, a food material for the pest and a pesticide. The composite material is formed by mixing a thermoplastic polymer, wood fragments or other cellulosic materials and a quantity of pesticide, and thereafter creating a molten material within a mixer, compounder, extruder or the like. The molten material is extruded or molded to form the desired shape.
1. A method of making a bait that is palatable to termites, the method comprising:
extruding a mixture of (i) cellulose acetate butyrate, (ii) alpha cellulose, and (iii) noviflumuron to form a composite material in which the alpha cellulose and noviflumuron are contained within a plastic structural matrix, and
cooling the composite material to a temperature to form the bait.
2. The method of claim 1 , further comprising adding a plasticizer to the mixture.
3. The method of claim 1 , further comprising adding a lubricant to the mixture.
4. The method of claim 1 , wherein extruding the mixture comprises feeding the mixture into a twin screw extruder.
5. The method of claim 1 , wherein the composite material includes about 5% to about 50% by weight of the plastic structural matrix.
6. The method of claim 1 , wherein the composite material includes about 50% to about 85% by weight of the alpha cellulose.
7. The method of claim 1 , wherein the composite material includes less than 5% by weight of noviflumuron.
8. The method of claim 1 , wherein the step of extruding has a processing temperature from about 130° C. to about 180° C.
9. The method of claim 1 , wherein the step of extruding has a processing temperature from about 110° C. to about 160° C.