Osteoinductive calcium phosphates
The invention relates to a porous osteoinductive calcium phosphate material having an average grain size in a range of 0.1-1.50 μm, having a porosity consisting essentially only of micropores in a size range of 0.1-1.50 μm, and having a surface area percentage of micropores in a range of 10-40%.
1. A porous osteoinductive calcium phosphate material having an average grain size in a range of 0.1-1.50 μm, a porosity comprising micropores in a size range of 0.1-1.50 μm and being free of macropores and having a surface area percentage of micropores in a range of 10-40% over a surface of the porous osteoinductive calcium phosphate material, the porous osteoinductive calcium phosphate material being osteoinductive in a non-osseous site, wherein the porous osteoinductive calcium phosphate material has a protein adsorption capacity, expressed as a percentage of protein absorbed by a volume of 1 ml of said calcium phosphate material from a volume of 3 ml of a 1% aqueous solution of fetal bovine serum (FBS) in the presence of 25 ppm sodium azide (NaN 3 ) after 24 hrs at 37° C., of at least 40%.
2. The porous osteoinductive calcium phosphate material according to claim 1 , wherein the porous osteoinductive calcium phosphate material is in the form of microparticles having a particle size ranging from about 50 μm to about 1500 μm.
3. The porous osteoinductive calcium phosphate material according to claim 2 , wherein the microparticles have a particle size ranging from about 200 μm to about 300 μm.
4. The porous osteoinductive calcium phosphate material according to claim 2 , wherein the microparticles have a particle size ranging from about 212 μm to 300 μm.
5. The porous osteoinductive calcium phosphate material according to claim 1 , wherein the calcium phosphate is chosen from the group consisting of octacalcium phosphate, apatites, whitlockites, and combinations thereof.
6. The porous osteoinductive calcium phosphate material according to claim 1 , wherein the calcium phosphate is resorbable biphasic calcium phosphate (BCP) or resorbable tricalcium phosphate.
7. The porous osteoinductive calcium phosphate material according to claim 1 for use as a medical implant material or tissue scaffold.
8. The porous osteoinductive calcium phosphate material according to claim 1 , wherein the porosity consists essentially only of micropores in the size range of 0.1-1.50 μm.
9. The porous osteoinductive calcium phosphate material according to claim 1 , wherein the non-osseous site comprises living tissues.
10. The porous osteoinductive calcium phosphate material according to claim 1 , wherein the porous osteoinductive calcium phosphate material is applied as a coating to another material.
11. The porous osteoinductive calcium phosphate material according to claim 1 , wherein the porosity is interconnected.