Process for producing polytetrafluoroethylene molding powder and process for producing polytetrafluoroethylene agglomerated product
View Patent ↗To provide a process for producing a PTFE molding powder having a high bulk density from granular polymer particles without using an emulsifying agent having problems of bioaccumulation and toxicity. A process for producing a polytetrafluoroethylene molding powder, which comprises a step of suspension-polymerizing a monomer containing at least 99.8 mass % of tetrafluoroethylene in an aqueous medium to produce granular polymer particles and a step of milling the granular polymer particles, wherein the aqueous medium contains a compound represented by R F (OCF(X 1 )CF 2 ) k-1 OCF(X 2 )COO − M + , at a concentration of from 0.5 to 2,000 ppm. R F is a perfluorinated C 1-10 monovalent organic group, X 1 and X 2 are fluorine atoms, etc., and M + is an ammonium ion or the like.
1. A process for producing a polytetrafluoroethylene molding powder, which comprises:
suspension-polymerizing a monomer consisting of tetrafluoroethylene in an aqueous medium to produce granular polymer particles and
milling the granular polymer particles to form the polytetrafluoroethylene molding powder,
wherein the aqueous medium contains a compound represented by the following formula (1) at a concentration of from 0.5 to 2,000 ppm:
R F (OCF(X 1 )CF 2 ) k-1 OCF(X 2 )COO − M + (1)
wherein R F is a perfluorinated C 1-10 monovalent organic group, each of X 1 and X 2 which are independent of each other, is a fluorine atom or a trifluoromethyl group, k is an integer of at least 1, and M + is a hydrogen ion, an ammonium ion, an alkyl-substituted ammonium ion or an alkali metal ion.
2. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the concentration of the compound represented by the formula (1) in the aqueous medium is from 0.5 to 50 ppm.
3. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the concentration of the compound represented by the formula (1) in the aqueous medium is from 100 to 2,000 ppm.
4. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the polytetrafluoroethylene molding powder has an average particle size of from 20 to 60 μm.
5. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein R F in the formula (1) is —CF 2 CF 3 or —CF 2 CF 2 CF 3 .
6. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein both X 1 and X 2 in the formula (1) are fluorine atoms.
7. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein k in the formula (1) is 2 or 3.
8. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the compound represented by the formula (1) is a compound represented by the following formula (1-3):
CF 3 CF 2 OCF 2 CF 2 OCF 2 COO − (NH 4 ) + (1-3),
9. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the aqueous medium has a pH of from 8 to 10.
10. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the step of milling the granular polymer particles is carried out by means of a cutter mill and/or a jet mill.
11. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the polytetrafluoroethylene molding powder has a bulk density of from 0.35 to 0.50 g/mL.
12. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the suspension-polymerizing is a homopolymerization of tetrafluoroethylene.
13. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the concentration of the compound represented by the formula (1) in the aqueous medium is from 150 to 1,200 ppm.
14. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the concentration of the compound represented by the formula (1) in the aqueous medium is from 0.9 to 30 ppm.
15. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the compound represented by the following formula (1) is at least one selected from the group consisting of CF 3 OCF 2 CF 2 OCF 2 COO − (NH 4 ) + , CF 3 (OCF 2 CF 2 ) 2 OCF 2 COO − (NH 4 ) + , CF 3 CF 2 OCF 2 CF 2 OCF 2 COO − (NH 4 ) + , CF 3 CF 2 (OCF 2 CF 2 ) 2 OCF 2 COO − (NH 4 ) + , CF 3 CF 2 CF 2 (OCF 2 CF 2 ) 2 OCF 2 COO − (NH 4 ) + , CF 3 CF 2 CF 2 OCF 2 CF 2 OCF 2 COO − (NH 4 ) + , and CF 3 (CF 2 ) 3 OCF 2 CF 2 OCF 2 COO − (NH 4 ) + .
16. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the compound represented by the following formula (1) is CF 3 CF 2 OCF 2 CF 2 OCF 2 COO − (NH 4 ) + .
17. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the polytetrafluoroethylene molding powder has a bulk density of from 0.41 to 0.45 g/mL according to JIS K6891.
18. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the compound represented by the following formula (1) is present during the suspension polymerizing at a concentration of from 150 to 1,200 ppm and the polytetrafluoroethylene molding powder formed by the suspension polymerizing has a bulk density of from 0.45 to 0.50 g/mL according to JIS K6891.
19. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , further comprising:
after the milling, agglomerating the polytetrafluoroethylene molding powder to form a polytetrafluoroethylene agglomerated product having a bulk density of from 0.80 to 1.00 g/mL according to JIS K6891.
20. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the polytetrafluoroethylene molding powder has a specific surface area of from 1.7 to 2.2 m 2 /g.
21. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the polytetrafluoroethylene molding powder has standard specific gravity of 2.157 to 2.168 according to ASTM D4894-98a.
22. The process for producing a polytetrafluoroethylene molding powder according to claim 1 , wherein the polytetrafluoroethylene molding powder has a dielectric breakdown voltage of film of from 11.5 to 12.8 kV/0.1 mm measured by packing the polytetrafluoroethylene molding powder in a mold and compression-molding at 25° C. at 15.7 MPa, followed by sintering by heating at 370° C. for 4 hours to obtain a molded product (fired column block) then subjecting the molded product to a dielectric breakdown voltage test in accordance with JIS K6891.
23. A process for producing a polytetrafluoroethylene agglomerated product, which comprises a step of agglomerating the polytetrafluoroethylene molding powder produced by the process as defined in claim 1 .
24. The process for producing a polytetrafluoroethylene agglomerated product according to claim 23 , wherein the step of agglomerating the polytetrafluoroethylene molding powder is carried out by a wet agglomeration method in a two phase liquid medium comprising water and an organic medium.
25. The process for producing a polytetrafluoroethylene agglomerated product according to claim 23 , wherein the polytetrafluoroethylene agglomerated product has an average particle size of from 300 to 500 μm.