PROCESS FOR PREFERENTIAL DISSOLUTION OF IRON IN THE PRESENCE OF TITANIUM
Disclosed herein are processes for selectively solubilizing iron from a substrate material containing both titanium and iron, such as ilmenite ore. In one embodiment, the process comprises contacting a substrate material comprising iron and titanium with an aqueous solution of an extractant selected from the group consisting of malonic acid, a malonic acid salt, citric acid, a citric acid salt, and mixtures thereof, at a temperature between about 25° C. and about 160° C. for a time sufficient to form an aqueous leachate comprising iron and titanium, and solids comprising titanium; wherein the leachate has a titanium content of 25 weight percent or less, based on the sum of the iron and the titanium contents of the leachate on a weight basis.
1 . A process comprising the step:
a) contacting a substrate material comprising iron and titanium with an aqueous solution of an extractant selected from the group consisting of malonic acid, a malonic acid salt, citric acid, a citric acid salt, and mixtures thereof, at a temperature between about 25° C. and about 160° C. for a time sufficient to form an aqueous leachate comprising iron and titanium, and solids comprising titanium;
wherein the leachate has a titanium content of 25 weight percent or less, based on the sum of the iron and the titanium contents of the leachate on a weight basis.
2 . The process of claim 1 , further comprising the steps:
b) separating the solids from the leachate to obtain separated solids; and
c) optionally, washing the separated solids with water.
3 . The process of claim 1 , wherein the substrate material comprises ilmenite ore.
4 . The process of claim 1 , wherein the substrate material comprises titanyl hydroxide cake.
5 . The process of claim 1 , wherein the substrate material comprises titanium dioxide pigment.
6 . The process of claim 5 , wherein the titanium dioxide pigment comprises rutile titanium dioxide, anatase titanium dioxide, or a mixture thereof.
7 . The process of claim 1 , wherein the aqueous solution has a concentration of the extractant between about 0.1 M and about 7.4 M.
8 . The process of claim 1 , wherein the aqueous solution of the extractant is present in an amount whereby the molar ratio of the extractant to the iron of the substrate material is between about 0.1:1 and about 500,000:1.
9 . The process of claim 1 , wherein the contacting is performed at a pressure between about 0.01 kPa and 1825 kPa.
10 . The process of claim 1 , wherein the contacting is performed in a continuous manner.
11 . The process of claim 1 , wherein the contacting is performed in a batch manner.
12 . The process of claim 1 , further comprising using the solids comprising titanium in a process for producing titanium dioxide pigment.
13 . The process of claim 2 , further comprising using the separated solids obtained in step b) or step c) in a process for producing titanium dioxide pigment.
14 . The process of claim 1 , wherein the extractant is citric acid.
15 . The process of claim 1 , wherein the extractant is malonic acid.
16 . The process of claim 15 , wherein the leachate has a titanium content of 9 weight percent or less.
17 . The process of claim 1 , wherein the leachate has a titanium content of 5 weight percent or less.
18 . The process of claim 1 , wherein the substrate material contains less than 0.1 weight percent iron.
19 . The process of claim 1 , wherein the substrate material contains from about 0.0001 weight percent iron to about 55 weight percent iron.
20 . The process of claim 2 , further comprising step d) recovering iron from the leachate obtained in step b).
21 . The process of claim 1 , wherein the extractant is malonic acid and the temperature is between about 50° C. and about 100° C., and wherein the aqueous solution has a concentration of malonic acid between about 3 M and about 7.4 M.
22 . A titanium-enriched material obtained by a process comprising the steps:
i) contacting a substrate material comprising iron and titanium with an aqueous solution of an extractant selected from the group consisting of malonic acid, a malonic acid salt, citric acid, a citric acid salt, and mixtures thereof, at a temperature between about 25° C. and about 160° C. for a time sufficient to form a leachate comprising iron and titanium, and solids comprising titanium;
wherein the leachate has a titanium content of 25 weight percent or less, based on the sum of the iron and the titanium contents of the leachate on a weight basis; and
ii) separating the solids from the leachate to obtain separated solids;
wherein the separated solids are titanium-enriched relative to the substrate material.