View Patent ↗An electrically conductive glass seal for providing a hermetic bond between an electrically conductive component and an insulator of a corona igniter is provided. The glass seal is formed by mixing glass frits, binder, expansion agent, and electrically conductive metal particles. The glass frits can include silica (SiO 2 ), boron oxide (B 2 O 3 ), aluminum oxide (Al 2 O 3 ), bismuth oxide (Bi 2 O 3 ), and zinc oxide (ZnO); the binder can include sodium bentonite or magnesium aluminum silicate, polyethylene glycol (PEG), and dextrin; the expansion agent can include lithium carbonate; and the electrically conductive particles can include copper. The finished glass seal includes the glass in a total amount of 50.0 to 85.0 weight (wt. %), and electrically conductive metal particles in an amount of 15.0 to 50.0 wt. %, based on the total weight of the glass seal.
1. A corona igniter, comprising:
an electrically conductive component;
an insulator surrounding said electrically conductive component;
an electrically conductive glass seal providing a hermetic bond between said electrically conductive component and said insulator;
said electrically conductive glass seal including at least one glass in a total amount of 50.0 to 85.0 wt. %, and electrically conductive metal particles in an amount of 15.0 to 50.0 wt. %, based on the total weight of said glass seal; wherein the glass seal includes gas-filled pores in an amount of 25.0 to 75.0 vol. %, based on the total volume of the glass seal; and said glass seal is electrical conductive.
2. The corona igniter of claim 1 , wherein said gas-filled pores are present in an amount of 35.0 to 45.0 vol. %, based on the total volume of said glass seal and said gas-filled pores are spaced from one another by said glass and said electrically conductive metal particles.
3. The corona igniter of claim 1 , wherein said glass seal has an electrically conductivity ranging from 9×10 6 S/m to 65×10 6 S/m.
4. The corona igniter of claim 1 , wherein said electrically conductive component includes a central electrode surrounded by said insulator, and a firing tip at an end of said central electrode, said firing tip including a plurality of branches each extending radially outwardly from a center axis.
5. The corona igniter of claim 1 , wherein said at least one glass includes silica (SiO 2 ), boron oxide (B 2 O 3 ), aluminum oxide (Al 2 O 3 ), bismuth oxide (Bi 2 O 3 ), and zinc oxide (ZnO); and said electrically conductive particles include copper.
6. The corona igniter of claim 1 , wherein said at least one glass includes silica (SiO 2 ) in an amount of 35.0 to 40.0 wt. %, boron oxide (B 2 O 3 ) in an amount of 20.0 to 28.0 wt. %, aluminum oxide (Al 2 O 3 ) in an amount of 10.0 to 15.0 wt. %, bismuth oxide (Bi 2 O 3 ) in an amount of 10.0 to 15.0 wt. %, and zinc oxide (ZnO) in an amount of 3.0 to 5.0 wt. %, based on the total weight of said at least one glass.
7. The corona igniter of claim 6 , wherein said at least one glass further include alkali metal oxides in a total amount of 2.0 to 6.0 wt. % and alkaline earth metal oxides in a total amount of 3.0 to 7.0 wt. %, based on the total weight of said at least one glass.
8. The corona igniter of claim 1 , wherein said gas-filled pores are present in an amount of 35.0 to 45.0 vol. %, based on the total volume of said glass seal.
9. The corona igniter of claim 1 , wherein said gas-filled pores are spaced from one another by said glass and said electrically conductive metal particles.
10. The corona igniter of claim 1 , wherein said electrically conductive metal particles include copper.
11. The corona igniter of claim 10 , wherein said electrically conductive metal particles include flakes of the copper and have a particle size of less than 45 microns.
12. The corona igniter of claim 1 , wherein said glass seal has an electrical conductivity above 30×10 6 S/m.