Corrosion and wear resistant coating on zirconium alloy cladding
View Patent ↗The invention relates to compositions and methods for coating a zirconium alloy cladding of a fuel element for a nuclear water reactor. The composition includes a master alloy including one or more alloying elements selected from chromium, silicon and aluminum, a chemical activator and an inert filler. The alloying element(s) is deposited or are co-deposited on the cladding using a pack cementation process. When the coated zirconium alloy cladding is exposed to and contacted with water in a nuclear reactor, a protective oxide layer can form on the coated surface of the cladding.
1. A method of coating a zirconium alloy substrate for use in a nuclear water reactor, comprising:
obtaining the zirconium alloy substrate having a surface;
combining a master alloy comprising one or more elements selected from the group consisting of chromium, silicon and aluminum, a chemical activator and an inert filler powder to form a coating mixture;
obtaining a chamber having a heating zone and an inert or reducing gas atmosphere;
surrounding the zirconium alloy substrate with the coating mixture in the chamber;
heating the chamber to an elevated temperature;
reacting the master alloy with the chemical activator to form a gaseous compound;
diffusing the gaseous compound to contact the surface of the zirconium alloy substrate;
decomposing the gaseous compound;
depositing the one or more elements of the master alloy on the surface of the zirconium alloy substrate; and
forming a substantially uniform diffusion coating layer thereon comprising zirconium and the one or more elements of the master alloy.
2. The method of claim 1 , wherein the surrounding includes packing the zirconium alloy substrate in a bed of the coating mixture.
3. The method of claim 1 , wherein the diffusion coating layer is formed on one or both of an interior surface and an exterior surface of the zirconium alloy substrate.
4. The method of claim 1 , further comprising:
positioning the zirconium alloy substrate with the substantially uniform diffusion coating layer thereon in a nuclear reactor;
exposing and contacting with water the zirconium alloy substrate with the substantially uniform diffusion coating layer thereon; and
forming a protective oxide layer on the substantially uniform diffusion coating layer, which comprises one or more of the following Cr 2 O 3 , SiO 2 , and Al 2 O 3 when the one or more elements of the master alloy is chromium, silicon and aluminum, respectively.
5. The method of claim 1 , wherein the diffusion coating layer comprises a Zr—Cr phase, a Zr—Si phase and a Zr—Al phase when the one or more elements of the master alloy is chromium, silicon and aluminum, respectively.
6. The method of claim 1 , wherein the heating is conducted at a temperature from 600° C. to 1100° C.
7. The method of claim 1 , wherein the substrate has a thickness from 1 micron to 200 microns.
8. The method of claim 7 , wherein the coated zirconium alloy substrate is subjected to one or more cold working steps to reduce the overall thickness and achieve a final dimension.
9. The method of claim 8 , wherein the cold working comprises pilgering.
10. The method of claim 8 , further comprising intermediate annealing of the coated zirconium alloy substrate to release residual stress in the coating and cladding.