Methods for producing solid ceramic particles using a microwave firing process
View Patent ↗Methods for producing solid, substantially round, spherical and sintered particles from a slurry of a raw material having an alumina content of greater than about 40 weight percent. The slurry is processed to prepare green pellets which are sintered in a furnace with microwave energy at a temperature of 1480 to 1520° C. to produce solid, substantially round, spherical and sintered particles having an average particle size greater than about 200 microns, a bulk density of greater than about 1.35 g/cm 3 , and an apparent specific gravity of greater than about 2.60.
1. A method for forming sintered substantially round and spherical pellets, comprising:
forming substantially round and spherical green pellets from raw materials comprising water and kaolin clay; and
sintering the green pellets in a microwave furnace at a temperature of from about 1480° C. to about 1520° C. for a time at peak temperature of from about 20 to about 45 minutes, to form a proppant having a bulk density of from about 1.35 to about 1.60 g/cm 3 and a crush percent at 7500 psi of from about 1.5 to about 3.5;
wherein the proppant has a bulk density and a crush percent at 7500 psi that is less than that of proppant made from the green pellets and sintered in a gas-fired rotary kiln.
2. The method of claim 1 , wherein the proppant has an apparent specific gravity of about 2.6 to about 2.8.
3. The method of claim 1 , wherein the green pellets have a moisture content of at least about 25% by weight.
4. The method of claim 1 , wherein the green pellets have a size of from 16 to 80 U.S. mesh.
5. The method of claim 1 , wherein the green pellets are sintered in the microwave furnace for about 50 to about 200 minutes.
6. The method of claim 1 , wherein the substantially round and spherical green pellets are prepared from a slurry having a solids content of from about 40 to about 60% by weight and having an alumina content in a range of from about 40 to about 55% by weight.
7. A method for producing sintered particles comprising:
preparing a slurry having a solids content of from about 40 to about 60% by weight, and comprising water and a raw material having an alumina content in a range of from about 40 to about 55% by weight;
atomizing the slurry into droplets;
coating seeds comprising alumina with the droplets to form green particles; and
sintering the green particles in a microwave furnace at a temperature of from about 1480° C. to about 1520° C. for a time at peak temperature of from about 20 to about 45 minutes, to form a proppant having a bulk density of from about 1.35 to about 1.60 g/cm 3 and a crush percent at 7500 psi of from about 1.5 to about 3.5;
wherein the proppant has a bulk density and a crush percent at 7500 psi that is less than that of proppant made from the green particles and sintered in a gas-fired rotary kiln.
8. The method of claim 7 , wherein the green particles are sintered for about 50 to about 200 minutes.
9. The method of claim 7 , further comprising adding to the slurry at least one of a pH adjusting reagent, a dispersant and a defoamer before atomizing the slurry.
10. The method of claim 7 , wherein atomizing the slurry comprises feeding the slurry to a fluidizer operable to atomize the slurry into droplets; and wherein the seeds are positioned in a particle bed in the fluidizer.
11. The method of claim 7 , further comprising drying the green particles before sintering.