Method for applying stable coating on silicone hydrogel contact lenses
The invention is related to a method for producing silicone hydrogel contact lenses with having a stable coating thereon. A method of the invention comprises a water-based coating process (step) for forming a relatively-stable base coating of a homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid onto a silicone hydrogel contact lens made from a lens formulation comprising from about 35% to about 60% by weight of N-vinylpyrrolidone.
1. A method for producing coated silicone hydrogel contact lenses each having a crosslinked hydrophilic coating thereon, comprising the steps of:
(a) obtaining a silicone hydrogel contact lens from a polymerizable composition comprising (i) at least one silicone-containing vinylic monomer or macromer, (ii) from about 35% to about 56% by weight of N-vinylpyrrolidone relative to the total amount of polymerizable components, and (iii) one or more hydrophilic vinylic monomers selected from the group consisting of N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, 2-acrylamidoglycolic acid, 3-acryloylamino-1-propanol, N-hydroxyethyl acrylamide, N-[tris(hydroxymethyl)methyl]-acrylamide, N-methyl-3-methylene-2-pyrrolidone, 1-ethyl-3-methylene-2-pyrrolidone, 1-methyl-5-methylene-2-pyrrolidone, 1-ethyl-5-methylene-2-pyrrolidone, 5-methyl-3-methylene-2-pyrrolidone, 5-ethyl-3-methylene-2-pyrrolidone, 1-n-propyl-3-methylene-2-pyrrolidone, 1-n-propyl-5-methylene-2-pyrrolidone, 1-isopropyl-3-methylene-2-pyrrolidone, 1-isopropyl-5-methylene-2-pyrrolidone, 1-n-butyl-3-methylene-2-pyrrolidone, 1-tert-butyl-3-methylene-2-pyrrolidone, 2-hydroxyethylmethacrylate, 2-hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, trimethylammonium 2-hydroxy propylmethacrylate hydrochloride, aminopropyl methacrylate hydrochloride, dimethylaminoethyl methacrylate, glycerol methacrylate, a C 1 -C 4 -alkoxy polyethylene glycol (meth)acrylate having a weight average molecular weight of up to 1500, methacrylic acid, N-vinyl formamide, N-vinyl acetamide, N-vinyl isopropylamide, N-vinyl-N-methyl acetamide, allyl alcohol, and mixtures thereof, wherein the silicone hydrogel contact lens has a polymer matrix containing polyvinylpyrrolidone segments; and
(b) contacting the silicone hydrogel contact lens with an aqueous solution of a homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid to form a base coating on the silicone hydrogel contact lens, wherein the aqueous solution of the homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid has a pH of from about 2.5 to about 5.5, wherein the homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid has a weight average molecular weight M w of at least about 50,000 Daltons and is polyacrylic acid, polymethacrylic acid, polyethylacrylic acid, polypropylacrlic acid, poly(acrylic acid-co-methacrylic acid), poly[(meth)acrylic acid-co-ethylacrylic acid], poly[(meth)acrylic acid-co-propylacrylic acid], poly[(meth)acrylic acid-co-acrylamide], poly[(meth)acrylic acid-co-vinylpyrrolidone], poly[ethylacrylic acid-co-acrylamide], poly[ethylacrylic acid-co-vinylpyrrolidone], poly[propylacrylic acid-co-acrylamide], poly[propylacrylic acid-co-vinylpyrrolidone], hydrolyzed poly[(meth)acrylic acid-co-vinylacetate], hydrolyzed poly[ethylacrylic acid-co-vinylacetate], hydrolyzed poly[propylacrylic acid-co-vinylacetate], or combinations thereof, wherein the polyvinylpyrrolidone segments of the polymer matrix form, with the homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid, strong interpolymer complexes which are stable as characterized by having a water-break-up-time (WBUT) of about 20 seconds or more after the silicone hydrogel contact lens with the base coating thereon has been autoclaved at 115° C. to 125° C. in a phosphate buffered saline having a pH from about 6.5 to about 7.5 for about 30 minutes.
2. The method of claim 1 , wherein the one or more hydrophilic vinylic monomers are selected from the group consisting of N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, 2-acrylamidoglycolic acid, 3-acryloylamino-1-propanol, N-hydroxyethyl acrylamide, N-[tris(hydroxymethyl)methyl]-acrylamide, 2-hydroxyethylmethacrylate, 2-hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, trimethylammonium 2-hydroxy propylmethacrylate hydrochloride, aminopropyl methacrylate hydrochloride, dimethylaminoethyl methacrylate, glycerol methacrylate, a C 1 -C 4 -alkoxy polyethylene glycol (meth)acrylate having a weight average molecular weight of up to 1500, methacrylic acid, N-vinyl acetamide, N-vinyl isopropylamide, N-vinyl-N-methyl acetamide, and mixtures thereof.
3. The method of claim 1 , wherein the polymerizable composition comprises from about 40% to about 52% by weight of N-vinylpyrrolidone relative to the total amount of polymerizable components.
4. The method of claim 1 , wherein the homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid is polyacrylic acid, polymethacrylic acid, polyethylacrylic acid, polypropylacrlic acid, poly(acrylic acid-co-methacrylic acid), poly[(meth)acrylic acid-co-ethylacrylic acid], poly[(meth)acrylic acid-co-propylacrylic acid], or combinations thereof.
5. The method of claim 4 , wherein the weight average molecular weight M w of the homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid for forming a base coating on silicone hydrogel contact lenses is from about 100,000 to about 5,000,000 Daltons.
6. The method of claim 5 , wherein the homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid is polyacrylic acid, polymethacrylic acid, or combinations thereof.
7. The method of claim 6 , wherein the method further comprises a step of covalently attaching and crosslinking a water-soluble and thermally-crosslinkable hydrophilic polymeric material having azetidinium groups onto the base coating to form a non-silicone hydrogel coating on the silicone hydrogel contact lens.
8. The method of claim 4 , further comprising a step of covalently attaching and crosslinking a water-soluble and thermally-crosslinkable hydrophilic polymeric material having azetidinium groups onto the base coating to form a non-silicone hydrogel coating on the silicone hydrogel contact lens.
9. The method of claim 8 , wherein the step of covalently attaching and crosslinking is carried out directly in a sealed lens package containing a packaging solution including the water-soluble, thermally crosslinkable hydrophilic polymeric material during sterilization by autoclave at a temperature from about 115° C. to about 125° C. for at least about 20 minutes.
10. The method of claim 8 , further comprising the steps of: contacting at room temperature the silicone hydrogel contact lens having the base coating thereon with an aqueous solution of a water-soluble thermally-crosslinkable hydrophilic polymeric material having azetidinium groups to form a top layer of the thermally-crosslinkable hydrophilic polymeric material on the surface of the silicone hydrogel contact lens; immersing the silicone hydrogel contact lens with the top layer of the thermally-crosslinkable hydrophilic polymeric material and the base coating thereon in a packaging solution in a lens package; sealing the lens package; and autoclaving at a temperature from about 115° C. to about 125° C. for at least about 20 minutes the lens package with the silicone hydrogel contact lens therein to form the non-silicone hydrogel coating on the silicone hydrogel contact lens.
11. The method of claim 2 , wherein the homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid is polyacrylic acid, polymethacrylic acid, polyethylacrylic acid, polypropylacrlic acid, poly(acrylic acid-co-methacrylic acid), poly[(meth)acrylic acid-co-ethylacrylic acid], poly[(meth)acrylic acid-co-propylacrylic acid], or combinations thereof.
12. The method of claim 11 , wherein the weight average molecular weight M w of a homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid for forming a base coating on silicone hydrogel contact lenses is from about 100,000 to about 5,000,000 Daltons.
13. The method of claim 12 , wherein the homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid is polyacrylic acid, polymethacrylic acid, polyethylacrylic acid, poly(acrylic acid-co-methacrylic acid), poly[(meth)acrylic acid-co-ethylacrylic acid], or combinations thereof.
14. The method of claim 13 , wherein the method further comprises a step of covalently attaching and crosslinking a water-soluble and thermally-crosslinkable hydrophilic polymeric material having azetidinium groups onto the base coating to form a non-silicone hydrogel coating on the silicone hydrogel contact lens.
15. The method of claim 11 , further comprising a step of covalently attaching and crosslinking a water-soluble and thermally-crosslinkable hydrophilic polymeric material having azetidinium groups onto the base coating to form a non-silicone hydrogel coating on the silicone hydrogel contact lens.
16. The method of claim 15 , wherein the step of covalently attaching and crosslinking is carried out directly in a sealed lens package containing a packaging solution including the water-soluble, thermally crosslinkable hydrophilic polymeric material during sterilization by autoclave at a temperature from about 115° C. to about 125° C. for at least about 20 minutes.
17. The method of claim 15 , further comprising the steps of: contacting at room temperature the silicone hydrogel contact lens having the base coating thereon with an aqueous solution of a water-soluble thermally-crosslinkable hydrophilic polymeric material having azetidinium groups to form a top layer of the thermally-crosslinkable hydrophilic polymeric material on the surface of the silicone hydrogel contact lens; immersing the silicone hydrogel contact lens with the top layer of the thermally-crosslinkable hydrophilic polymeric material and the base coating thereon in a packaging solution in a lens package; sealing the lens package; and autoclaving at a temperature from about 115° C. to about 125° C. for at least about 20 minutes the lens package with the silicone hydrogel contact lens therein to form the non-silicone hydrogel coating on the silicone hydrogel contact lens.
18. The method of claim 3 , wherein the homo- or copolymer of acrylic acid or C 1 -C 3 alkylacrylic acid has a weight average molecular weight M w of from about 100,000 to about 5,000,000 Daltons and is polyacrylic acid, polymethacrylic acid, polyethylacrylic acid, polypropylacrlic acid, poly(acrylic acid-co-methacrylic acid), poly[(meth)acrylic acid-co-ethylacrylic acid], poly[(meth)acrylic acid-co-propylacrylic acid], or combinations thereof.
19. The method of claim 18 , wherein the method further comprises a step of covalently attaching and crosslinking a water-soluble and thermally-crosslinkable hydrophilic polymeric material having azetidinium groups onto the base coating to form a non-silicone hydrogel coating on the silicone hydrogel contact lens.
20. The method of claim 19 , wherein the step of covalently attaching and crosslinking is carried out directly in a sealed lens package containing a packaging solution including the water-soluble, thermally crosslinkable hydrophilic polymeric material during sterilization by autoclave at a temperature from about 115° C. to about 125° C. for at least about 20 minutes.