Transparent, tough and heatproof rubber composition comprising neodymium-catalyzed isoprene component, and manufacturing process for the same
View Patent ↗In order to provide a rubber composition having high transparency, toughness and heat-resisting property, the present invention can provide a composition comprising a neodymium-catalyzed isoprene rubber (IR) component; and a rubber polymer (RB) component selected from the group consisting of BR, 1,2-polybutadiene rubber, and SBR, wherein the amount of IR is from about 5 to 95 mass parts with the proviso that the total amount of IR and RB is 100 mass parts, wherein the composition is substantially free of silica, wherein the composition has haze of less than about 20%, and wherein the composition has Type A Durometer hardness (0 sec) of about 30 or more.
1. A transparent, crosslinked rubber composition, comprising:
a neodymium-catalyzed isoprene rubber (IR) component; and
a rubber polymer component selected from the group consisting of butadiene rubber (BR), 1,2-polybutadiene rubber, and styrene butadiene rubber (SBR),
wherein the amount of the neodymium-catalyzed isoprene rubber is from 5 to 95 mass parts, with the proviso that the total amount of the neodymium-catalyzed isoprene rubber and the rubber polymer component is 100 mass parts,
wherein the composition is substantially free of silica,
wherein the composition has haze of less than 20%, on 2 mm thick sheet, measured according to JIS K7136,
wherein the composition has Type A Durometer hardness (0 sec) of 30 or more, measured according to JIS K6253;
wherein the neodymium-catalyzed isoprene rubber has a cis content of 95% or more.
2. The composition according to claim 1 , wherein the absolute value of the difference between the refractive indices of the neodymium-catalyzed isoprene rubber and the rubber polymer component is 0.100 or less.
3. The composition according to claim 1 , wherein the rubber polymer component includes low-cis polybutadiene rubber.
4. The composition according to claim 1 , wherein the rubber polymer component includes syndiotactic 1,2-polybutadiene rubber.
5. The composition according to claim 1 , wherein the composition is substantially free of oil as a softener.
6. The composition according to claim 1 , wherein the composition has Type A Durometer hardness (30 sec) which is 80% or more of the Type A Durometer hardness (0 sec), measured according to JIS K6253.
7. The composition according to claim 1 , wherein the composition has Tear Strength of 10 N/mm or more, measured on a 2-mm sheet according to JIS K6252.
8. The composition according to claim 1 , wherein the composition has Total Light Transmittance of 88% or more, measured according to JIS K7361-1.
9. The composition according to claim 1 , wherein the composition has haze of less than 20%, on 2 mm thick sheet heated at 70 degree C. for 72 hours, measured according to JIS K7136.
10. The composition according to claim 1 , wherein the neodymium-catalyzed isoprene rubber component includes 10,000 ppm or less of iron (in terms of metal iron), and/or 10,000 ppm or less of lithium (in terms of metal lithium).
11. A process for manufacturing a transparent, crosslinked rubber composition, being substantially free of silica, the process comprising the acts of:
providing a neodymium-catalyzed isoprene rubber polymer having the refractive index of between 1.500 to 1.525 at 23 degree C.;
providing a rubber polymer selected from the group consisting of butadiene rubber, 1,2-polybutadiene rubber, and styrene butadiene rubber, wherein the rubber polymer has the refractive index of between 1.500 to 1.525 at 23 degree C.;
mixing the neodymium-catalyzed isoprene rubber polymer and the rubber polymer such that the amount of the neodymium-catalyzed isoprene rubber polymer is from 5 to 95 mass parts, with the proviso that the total amount of the neodymium-catalyzed isoprene rubber polymer and the rubber polymer is 100 mass parts, to obtain a mixture thereof;
adding a crosslinker to the mixture; and
uniformly kneading the mixture;
wherein the neodymium-catalyzed isoprene rubber has a cis content of 95% or more.
12. The process according to claim 11 , wherein the crosslinker is peroxide.
13. An article comprising the composition according to claim 1 .
14. The article according to claim 13 , wherein the article is selected from the group consisting of footwear, tires, clothes, rain gears, eyewear, medical goggles, masks, medical masks, medical air tents, toys, damping materials, building materials, coatings for wiring, packaging materials, protective members for computers, computer peripherals, contraceptive devices, sex toys, artificial nipples, paper diapers, stationery, containers, food trays, balls for sports, ball chairs, and protection films.