EFFECT PIGMENTS
The present invention relates to effect pigments which are based on flake-form substrates having a circular form factor of 1.2-2 and are coated with at least one high-refractive-index layer, and to the use thereof, inter alia in paints, coatings, printing inks, plastics and in cosmetic formulations.
1 . An effect pigment comprising a flake-form substrate having a circular form factor of circumference 2 /area standardized to a circle of 1.2-2 coated with at least one high-refractive-index layer having a refractive index of n≧1.8.
2 . The effect pigment according to claim 1 , wherein the substrate has a circular form factor of 1.2-1.8.
3 . The effect pigment according to claim 1 , wherein the substrate has a particle size of 5-60 μm.
4 . The effect pigment according to one or more of claim 1 , wherein the substrate has a thickness of 0.2-0.6 μm.
5 . The effect pigment according to one or more of claim 1 , wherein the flake-form substrate is synthetic mica flakes, natural mica flakes, SiO 2 flakes, Al 2 O 3 flakes, glass flakes, iron oxide flakes, graphite flakes, TiO 2 flakes or mixtures thereof.
6 . The effect pigment according to claim 1 , wherein the flake-form substrate is a mica or glass flake.
7 . The effect pigment according to claim 1 , wherein the flake-form substrate is a natural mica flake.
8 . The effect pigment according to claim 1 , wherein the high-refractive-index layer is a compound that is at least one metal oxide, metal sulfide, iron titanate, iron oxide hydrate, titanium suboxide, metal, or mixtures or mixed phases of said compound.
9 . The effect pigment according to claim 1 , wherein the high-refractive-index layer comprises at least one compound that is TiO 2 , BiOCl, Ce 2 O 3 , Cr 2 O 3 , CoO, Co 3 O 4 , Fe 2 O 3 , Fe 3 O 4 , FeOOH, NiO, SnO 2 , VO 2 , V 2 O 3 , ZrO 2 , ZnO, CoAl 2 O 4 , BiVO 4 , iron titanates, iron oxide hydrates, Ti 3 O 5 , Ti 2 O 3 , TiO, Ce 2 S 3 , MoS 2 , aluminium, chromium, nickel, silver, gold, titanium, copper or alloys thereof or mixtures or mixed phases of said compounds with one another.
10 . The effect pigment according to claim 1 , wherein the high-refractive-index layer comprises one or more metal oxides.
11 . The effect pigment according to claim 1 , wherein the substrate is coated with at least one high-refractive-index layer having a refractive index n≧1.8 and at least one low-refractive-index layer having an n<1.8.
12 . The effect pigment according to claim 11 , wherein the low-refractive-index layer is SiO 2 , Al 2 O 3 , AlO(OH), MgF 2 .
13 . The effect pigment according to claim 1 , having the following layer sequence:
substrate flake+TiO 2 (anatase)
substrate flake+SnO 2 +TiO 2 (rutile)
substrate flake+TiO 2 +alkaline-earth metal titanate
substrate flake+SnO 2 +TiO 2 +alkaline-earth metal titanate
substrate flake+TiO 2 +Fe 2 O 3
substrate flake+SnO 2 +TiO 2 +Fe 2 O 3
substrate flake+TiO 2 +Fe 3 O 4
substrate flake+SnO 2 +TiO 2 +Fe 3 O 4
substrate flake+TiO 2 +Cr 2 O 3
substrate flake+SnO 2 +TiO 2 +Cr 2 O 3
substrate flake+TiO 2 +Carmine Red
substrate flake+SnO 2 +TiO 2 +Carmine Red
substrate flake+TiO 2 +Berlin Blue
substrate flake+SnO 2 +TiO 2 +Berlin Blue
substrate flake+TiO 2 /Fe 2 O 3
substrate flake+SnO 2 +TiO 2 /Fe 2 O 3
substrate flake+TiO 2 +SiO 2 +TiO 2
substrate flake+SnO 2 +TiO 2 +SiO 2 +SnO 2 +TiO 2
substrate flake+Fe 2 O 3
substrate flake+Fe 3 O 4
substrate flake+TiO 2 +SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SnO 2 +TiO 2 +SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+TiO 2 +SiO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SnO 2 +TiO 2 +SiO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SnO 2 +TiO 2 +SiO 2 +SnO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+TiO 2 /Fe 2 O 3 +SiO 2 +SnO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2
substrate flake+TiO 2 /Fe 2 O 3 +SiO 2 +SnO 2 +TiO 2
substrate flake+TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+TiO 2 +SiO 2 +Fe 3 O 4
substrate flake+TiO 2 +SiO 2 +Cr 2 O 3
substrate flake+Cr 2 O 3
substrate flake+Ag
substrate flake+Au
substrate flake+Fe 2 O 3 +SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +TiO 2 (anatase)
substrate flake+SiO 2 +SnO 2 +TiO 2 (rutile)
substrate flake+SiO 2 +TiO 2 +alkaline-earth metal titanate
substrate flake+SiO 2 +SnO 2 +TiO 2 +alkaline-earth metal titanate
substrate flake+SiO 2 +TiO 2 +Fe 2 O 3
substrate flake+SiO 2 +SnO 2 +TiO 2 +Fe 2 O 3
substrate flake+SiO 2 +TiO 2 +Fe 3 O 4
substrate flake+SiO 2 +SnO 2 +TiO 2 +Fe 3 O 4
substrate flake+SiO 2 +TiO 2 +Cr 2 O 3
substrate flake+SiO 2 +SnO 2 +TiO 2 +Cr 2 O 3
substrate flake+SiO 2 +TiO 2 +Carmine Red
substrate flake+SiO 2 +SnO 2 +TiO 2 +Carmine Red
substrate flake+SiO 2 +TiO 2 +Berlin Blue
substrate flake+SiO 2 +SnO 2 +TiO 2 +Berlin Blue
substrate flake+SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +SnO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +TiO 2 +SiO 2 +TiO 2
substrate flake+SiO 2 +SnO 2 +TiO 2 +SiO 2 +SnO 2 +TiO 2
substrate flake+SiO 2 +Fe 2 O 3
substrate flake+SiO 2 +Fe 3 O 4
substrate flake+SiO 2 +TiO 2 +SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +SnO 2 +TiO 2 +SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +TiO 2 +SiO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +SnO 2 +TiO 2 +SiO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +SnO 2 +TiO 2 +SiO 2 +SnO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +TiO 2 /Fe 2 O 3 +SiO 2 +SnO 2 +TiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2
substrate flake+SiO 2 +TiO 2 /Fe 2 O 3 +SiO 2 +SnO 2 +TiO 2
substrate flake+SiO 2 +TiO 2 /Fe 2 O 3 +SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +TiO 2 +SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+SiO 2 +TiO 2 +SiO 2 +Fe 3 O 4
substrate flake+SiO 2 +TiO 2 +SiO 2 +Cr 2 O 3
substrate flake+SiO 2 +Cr 2 O 3
substrate flake+SiO 2 +Ag
substrate flake+SiO 2 +Au
substrate flake+SiO 2 +Fe 2 O 3 +SiO 2 +TiO 2 /Fe 2 O 3
substrate flake+TiO 2 (anatase)+SiO 2 or
substrate flake+SnO 2 +TiO 2 (rutile)+SiO 2 .
14 . The effect pigment according to claim 1 , that is aftertreated with an organic and/or inorganic layer in order to increase light, water and weather stability.
15 . A process for the preparation of an effect pigment according to claim 1 , comprising grinding substrates in the form of lumps or coarse flakes to form substrate flakes having a diameter of 50-200 μm, subsequently introducing said flakes into a comminution machine, and adding water and/or an organic solvent, and treating a suspension thus formed mechanically for a number of hours in the comminution machine, during which the surface of the flakes is polished, maintaining mechanical loading of the substrate particles during communition so that a permanent shear results in further gentle delamination of particles and in smoothing of the edges and surfaces and a narrowed particle-size distribution is achieved by a subsequent classification in the form of a plurality of sedimentations.
16 . The process according to claim 15 , wherein the narrowed particle-size distribution is 5-60 μm.
17 . In paints, automotive paints, industrial coatings, coatings, powder coatings, printing inks, plastics, button pastes, ceramic materials, glasses, colored seed, absorbers in the laser marking of plastics, glasses, cardboard, paper, absorbers in the laser welding of plastics, colored food or pharmaceutical products, colored coatings on food or pharmaceutical products, cosmetic formulations, or anti-counterfeiting-elements in documents of value comprising an effect pigment, the improvement wherein the effect pigment is one according to claim 1 .
18 . A pigment composition comprising an effect pigment according to claim 1 and at least one absorbent, astringent, antimicrobial substance, antioxidant, antiperspirant, antifoaming agent, antidandruff active ingredient, antistatic, binder, biological additive, bleaching agent, chelating agent, deodorant, emollient, emulsifier, emulsion stabiliser, dye, humectant, film former, filler, odor substance, flavor substance, insect repellent, preservative, anticorrosion agent, cosmetic oil, solvent, oxidant, vegetable constituent, buffer substance, reducing agent, surfactant, propellant gas, opacifier, UV filter and UV absorber, denaturing agent, viscosity regulator, perfume or vitamin.
19 . A pigment composition comprising one or more binders, optionally one or more additives and at least one effect pigment according to claim 1 .
20 . A dry preparation comprising at least one effect pigment according to claim 1 .