Granted Patent B2

US 9,783,419 · App. 14/864,731 · Granted Oct 10, 2017

Abstract

Claims (43)

1. A phosphorous pentoxide producing method comprising:

forming pre-feed agglomerates containing phosphate ore particles, carbonaceous material particles, and silica particles;

heating the pre-feed agglomerates in a reducing or inert atmosphere to an induration temperature from above 900 C to less than 1180 C and maintaining the induration temperature for 15 minutes or more;

forming feed agglomerates and increasing a compression strength of the feed agglomerates to above 25 lb f using the heating, the feed agglomerates exhibiting a calcium-to-silica mole ratio less than 1 and a silica-to-(calcium+magnesium) mole ratio greater than 2;

forming a reducing kiln bed using the feed agglomerates; and

generating kiln off-gas and collecting phosphorous pentoxide from the kiln off gas.

2. The method of claim 1 , wherein the crush strength is above 50 lb f .

3. The method of claim 1 , wherein the heating occurs in an induration kiln selected from the group consisting of a tunnel kiln, a rotary co-current kiln, and a rotary counter-current kiln.

4. The method of claim 1 , wherein the heating occurs in a grate heater.

5. The method of claim 1 , wherein the induration temperature is from 930 to 1125 C.

6. The method of claim 1 , wherein the induration temperature is maintained for 30 to 90 minutes.

7. The method of claim 1 , further comprising pre-heating the pre-feed agglomerates in a grate heater to a pre-heat temperature from 950 C to less than 1180 C before the heating at the induration temperature, which occurs in an induration kiln.

8. The method of claim 1 , wherein the pre-feed agglomerates further contain clay particles and further comprising preparing the phosphate ore particles, carbonaceous material particles, clay particles, and silica particles such that 80% or more exhibit a size less than 200 mesh.

9. The method of claim 7 , further comprising:

scrubbing the kiln off-gas in a product acid scrubber and generating a scrubber off-gas;

making the scrubber off-gas reducing; and

using the reducing scrubber off-gas for the pre-heating in the grate heater.

10. The method of claim 1 , further comprising adding over bed air through a plurality of ports along the bed length, the over bed air entering kiln freeboard through a plurality of standpipes extending from respective ports to a height above the bed.

11. The method of claim 1 , wherein the pre-feed agglomerates comprise one or more contaminants selected from the group consisting of Al, As, Cd, Cl, Pb, and Hg and wherein the method further comprises decreasing a concentration of the contaminants in the feed agglomerates using the heating when compared to the pre-feed agglomerates.

12. A phosphorous pentoxide producing method comprising:

forming green agglomerates containing phosphate ore particles, carbonaceous material particles, silica particles, and a polymer;

drying the green agglomerates at a drying temperature from 40 to 300 C, the dried agglomerates exhibiting a compression strength above 25 lb f ;

heating the dried agglomerates in a reducing or inert atmosphere to an induration temperature from above 900 to less than 1180 C and maintaining the induration temperature for 15 minutes or more;

forming feed agglomerates and increasing a compression strength of the feed agglomerates to above 50 lb f using the heating, the feed agglomerates exhibiting a calcium-to-silica mole ratio less than 1 and a silica-to-(calcium+magnesium) mole ratio greater than 2;

forming a reducing kiln bed using the feed agglomerates; and

generating kiln off-gas and collecting phosphorous pentoxide from the kiln off gas.

13. The method of claim 12 , wherein the crush strength is above 100 lb f .

14. The method of claim 12 , wherein the induration temperature is from 950 to 1100 C and is maintained for 30 minutes or more.

15. The method of claim 12 , wherein the drying temperature is from 40 to 150 C and the green agglomerates further contain clay particles.

16. The method of claim 12 , wherein the polymer comprises a compound selected from the group consisting of acrylics, silicones, cross-linkable polyimides, epoxies, silicates of sodium, potassium, or lithium, and a combination of organic and inorganic polymers.

17. The method of claim 12 , wherein the polymer comprises Na 2 (SiO 2 ) n O.

18. The method of claim 12 , wherein the dried agglomerates comprise one or more contaminants selected from the group consisting of Al, As, Cd, Cl, Pb, and Hg and wherein the method further comprises decreasing a concentration of the contaminants in the feed agglomerates using the heating when compared to the dried agglomerates.

19. The method of claim 12 , further comprising preparing the phosphate ore particles, carbonaceous material particles, and silica particles such that 80% or more exhibit a size less than 200 mesh.

20. A phosphorous pentoxide producing method comprising:

extruding a material to form green agglomerates containing phosphate ore particles, carbonaceous material particles, silica particles, and 2 to 5 wt % (dry basis) clay particles;

drying the extruded, green agglomerates at a drying temperature from 40 to 150 C, the dried agglomerates exhibiting a compression strength above 50 lb f ;

heating the dried agglomerates in a reducing or inert atmosphere to an induration temperature from above 900 to less than 1180 C and maintaining the induration temperature for 15 minutes or more;

forming feed agglomerates and increasing a compression strength of the feed agglomerates to above 200 lb f using the heating, the feed agglomerates exhibiting a calcium-to-silica mole ratio less than 1 and a silica-to-(calcium+magnesium) mole ratio greater than 2;

forming a reducing kiln bed using the feed agglomerates; and

generating kiln off-gas and collecting phosphorous pentoxide from the kiln off gas.

21. The method of claim 20 , wherein the induration temperature is from 1000 to 1100 C and is maintained for 30 to 90 minutes.

22. The method of claim 20 , further comprising preparing the phosphate ore particles, carbonaceous material particles, clay particles, and silica particles such that 80% or more exhibit a size less than 325 mesh.

23. The method of claim 20 , wherein the dried agglomerates comprise one or more contaminants selected from the group consisting of Al, As, Cd, Cl, Pb, and Hg, wherein the induration temperature is maintained for 60 minutes or more, and wherein the method further comprises decreasing a concentration of the contaminants in the feed agglomerates using the heating when compared to the dried agglomerates.