Heat-curable powder coating composition
View Patent ↗The invention relates to a one component heat curable powder coating composition comprising a resin containing reactive unsaturations and wherein all said reactive unsaturations are carbon carbon double bonds connected directly to an electron withdrawing group, a thermal initiation system comprising a peroxide chosen from the group of compounds represented by formula (1) wherein R 1 and R 2 each independently stand for an optionally substituted alkyl of 1 to 30 C-atoms, wherein the 1 to 30 C-atoms do not include the C-atoms of the substituents or for an optionally substituted aryl of 6 to 18 C-atoms, wherein the 6 to 18 C-atoms do not include the C-atoms of the substituents, and a co-crosslinker chosen from the group of vinylethers, vinyletherurethanes, vinylesters, vinylamides, itaconates, enamines, vinylureas and mixtures thereof.
1. A one component heat curable powder coating composition comprising:
(i) a polyester resin containing reactive unsaturations, the polyester resin having a weight per the reactive unsaturations (WPU) as determined using 1 H-NMR which is higher than 250 and lower than 1500 g/mole,
(ii) a thermal initiation system comprising a peroxide chosen from the group consisting of compounds represented by formula (1)
wherein
R 1 and R 2 each independently stand for an optionally substituted alkyl of 1 to 30 C-atoms, wherein the 1 to 30 C-atoms do not include the C-atoms of the substituents or for an optionally substituted aryl of 6 to 18 C-atoms, and wherein the 6 to 18 C-atoms do not include the C-atoms of the substituents, and
(iii) a co-crosslinker having a weight per unsaturation (WPU) as determined using 1 H-NMR higher than 150 and lower than 870 g/mole, said crosslinker being chosen from the group consisting of vinylethers, vinyletherurethanes, vinylesters, vinylamides, itaconates, enamines, vinylureas and mixtures thereof, wherein
all of the reactive unsaturations are carbon-carbon double bonds connected directly to an electron withdrawing group and are reactive towards radicals generated by the peroxide, and wherein
the thermal initiation system is present in an amount such that when the powder coating composition is applied to a substrate and cured at a temperature of 130° C. for 20 minutes, the resulting coating resists at least 50 acetone double rubs (ADR), wherein each ADR is a back and forward movement over a surface of the coating having a thickness of approximately 60 μm using a cotton cloth drenched in acetone covering a hammer head having a weight of 980 grams and a contact surface area with the coating of 2 cm 2 .
2. The composition according to claim 1 , wherein the resin has a WPU higher than 250 and less than 1150 g/mole.
3. The composition according to claim 1 , wherein the resin has a WPU higher than 500 and less than 1500 g/mole.
4. The composition according to claim 1 , wherein the resin has a WPU higher than 500 and less than 1150 g/mole.
5. The composition according to claim 1 , wherein the co-crosslinker has a WPU higher than 150 and lower than 650 g/mole.
6. The composition according to claim 1 , wherein the co-crosslinker has a WPU higher than 150 and lower than 630 g/mole.
7. The composition according to claim 1 , wherein the resin has a hydroxyl value in the range of from 0 to 70 mg KOH per g resin.
8. The composition according to claim 1 , wherein the reactive unsaturations of the resin are based on maleic acid, fumaric acid, itaconic acid, acrylic acid and/or methacrylic acid.
9. The composition according to claim 1 , wherein the reactive unsaturations of the resin are based on maleic acid, fumaric acid, citraconic acid, itaconic acid, and/or mesaconic acid.
10. The composition according to claim 1 , wherein the reactive unsaturations of the resin are based on fumaric acid and/or maleic acid.
11. The composition according to claim 1 , wherein the reactive unsaturations of the resin are based on fumaric acid.
12. The composition according to claim 1 , wherein the peroxide is benzoyl peroxide or lauroyl peroxide.
13. The composition according to claim 1 , wherein the co-crosslinker is chosen from the group of vinylethers, vinylesters and mixtures thereof.
14. The composition according to claim 13 , wherein the co-crosslinker is a vinylether.
15. The composition according to claim 13 , wherein the resin has an acid value of less than 10 mg KOH per g resin.
16. The composition according to claim 14 , wherein the resin has an acid value of less than 10 mg KOH per g resin.
17. The composition according to claim 13 , wherein the resin has an acid value of less than 5 mg KOH per g resin.
18. The composition according to claim 14 , wherein the resin has an acid value of less than 5 mg KOH per g resin.
19. The composition according to claim 1 , wherein the composition further comprises an inhibitor.
20. The composition according to claim 19 , wherein the inhibitor is a hydroquinone or a catechol.
21. The composition according to claim 1 , wherein the resin has a glass transition temperature of at least 40° C. as measured via DSC at a heating rate of 5° C./min.
22. The composition according to claim 1 , wherein the resin has a glass transition temperature of at least 45° C. as measured via DSC at a heating rate of 5° C./min.
23. The composition according to claim 1 , wherein the resin has a glass transition temperature of at least 40 and of at most 65° C. as measured via DSC at a heating rate of 5° C./min.
24. The composition according to claim 1 , wherein the resin has a number average molecular weight in the range of from 1500 to 8000 Da.
25. The composition according to claim 1 , wherein the resin has a number average molecular weight in the range of from 2100 to 4000 Da.
26. The composition according to claim 1 , wherein
the reactive unsaturations of the resin are based on maleic acid, fumaric acid, itaconic acid, acrylic acid and/or methacrylic acid, said resin has a hydroxyl value in the range of from 0 to 70 mg KOH per g resin and a number average molecular weight in the range of from 1500 to 8000 Da and a glass transition temperature of at least 40° C. as measured via DSC at a heating rate of 5° C./min; and
the co-crosslinker has a WPU higher than 150 and lower than 630 g/mole and said co-crosslinker is chosen from the group of vinylethers, vinylesters and mixtures thereof.
27. The composition according to claim 1 , wherein
the reactive unsaturations of the resin are based on maleic acid, fumaric acid, itaconic acid, acrylic acid and/or methacrylic acid, said resin has a hydroxyl value in the range of from 0 to 70 mg KOH per g resin and an acid value of less than 10 mg KOH per g resin, and a number average molecular weight in the range of from 1500 to 8000 Da and a glass transition temperature of at least 40° C. as measured via DSC at a heating rate of 5° C./min; and
the co-crosslinker has a WPU higher than 150 and lower than 630 g/mole and said co-crosslinker is a vinylether; and
the composition comprises an inhibitor.
28. The composition according to claim 27 , wherein the reactive unsaturations of the resin are based on fumaric acid and/or maleic acid.
29. The composition according to claim 28 , wherein the reactive unsaturations of the resin are based on fumaric acid and/or maleic acid.
30. The composition according to claim 1 , wherein
the reactive unsaturations of the resin are based on maleic acid, fumaric acid, itaconic acid, acrylic acid and/or methacrylic acid, said resin has a hydroxyl value in the range of from 0 to 70 mg KOH per g resin and a number average molecular weight in the range of from 1500 to 8000 Da and a glass transition temperature of at least 40° C. as measured via DSC at a heating rate of 5° C./min; and
the co-crosslinker has a WPU higher than 150 and lower than 630 g/mole and said co-crosslinker is chosen from the group of vinylethers, vinylesters and mixtures thereof; and
the composition comprises an inhibitor.
31. The composition according to claim 30 , wherein the reactive unsaturations of the resin are based on fumaric acid and/or maleic acid.
32. The composition according to claim 1 , wherein
the reactive unsaturations of the resin are based on maleic acid, fumaric acid, itaconic acid, acrylic acid and/or methacrylic acid, said resin has a hydroxyl value in the range of from 0 to 70 mg KOH per g resin and a number average molecular weight in the range of from 1500 to 8000 Da and a glass transition temperature of at least 40° C. as measured via DSC at a heating rate of 5° C./min; and
the co-crosslinker has a WPU higher than 150 and lower than 630 g/mole and said co-crosslinker is a vinylether; and
the composition comprises an inhibitor.
33. The composition according to claim 32 , wherein the reactive unsaturations of the resin are based on fumaric acid and/or maleic acid.
34. The composition according to claim 1 , wherein
the reactive unsaturations of the resin are based on maleic acid, fumaric acid, itaconic acid, acrylic acid and/or methacrylic acid, said resin has a hydroxyl value in the range of from 0 to 70 mg KOH per g resin and an acid value of less than 10 mg KOH per g resin, and a number average molecular weight in the range of from 1500 to 8000 Da and a glass transition temperature of at least 40° C. as measured via DSC at a heating rate of 5° C./min; and
the co-crosslinker has a WPU higher than 150 and lower than 630 g/mole and said co-crosslinker is a vinylether.
35. The composition according to claim 34 , wherein the reactive unsaturations of the resin are based on fumaric acid and/or maleic acid.
36. The composition according to claim 1 , wherein
the reactive unsaturations of the resin are based on maleic acid, fumaric acid, itaconic acid, acrylic acid and/or methacrylic acid, said resin has a hydroxyl value in the range of from 0 to 70 mg KOH per g resin and an acid value of less than 5 mg KOH per g resin, and a number average molecular weight in the range of from 1500 to 8000 Da and a glass transition temperature of at least 40° C. as measured via DSC at a heating rate of 5° C./min; and
the co-crosslinker has a WPU higher than 150 and lower than 630 g/mole and said co-crosslinker is a vinylether.
37. The composition according to claim 36 , wherein the reactive unsaturations of the resin are based on fumaric acid and/or maleic acid.
38. The composition according to claim 1 , wherein
the reactive unsaturations of the resin are based on maleic acid, fumaric acid, itaconic acid, acrylic acid and/or methacrylic acid, said resin has a hydroxyl value in the range of from 0 to 70 mg KOH per g resin and a number average molecular weight in the range of from 1500 to 8000 Da and a glass transition temperature of at least 40° C. as measured via DSC at a heating rate of 5° C./min; and
the co-crosslinker has a WPU higher than 150 and lower than 630 g/mole and said co-crosslinker is a vinylether.
39. The composition according to claim 38 , wherein the reactive unsaturations of the resin are based on fumaric acid and/or maleic acid.
40. The composition according to claim 1 , wherein
the reactive unsaturations of the resin are based on maleic acid, fumaric acid, itaconic acid, acrylic acid and/or methacrylic acid, said resin has a hydroxyl value in the range of from 0 to 70 mg KOH per g resin and an acid value of less than 5 mg KOH per g resin, and a number average molecular weight in the range of from 1500 to 8000 Da and a glass transition temperature of at least 40° C. as measured via DSC at a heating rate of 5° C./min; and
the co-crosslinker has a WPU higher than 150 and lower than 630 g/mole and said co-crosslinker is a vinylether; and
the composition comprises an inhibitor.
41. The composition according to claim 40 , wherein the reactive unsaturations of the resin are based on fumaric acid and/or maleic acid.
42. A process for the preparation of a powder coating composition according to claim 1 comprising the steps of:
(a) mixing the components of the powder coating composition to obtain a premix;
(b) heating the premix to obtain an extrudate;
(c) cooling down the extrudate to obtain a solidified extrudate; and
(d) breaking the solidified extrudate into smaller particles to obtain the powder coating composition.
43. A process for coating a substrate comprising the following steps:
(1) applying a powder coating composition according to claim 1 to a substrate; and
(2) heating the substrate.
44. A substrate that is fully or partially coated with a powder coating composition according to claim 1 .
45. The substrate according to claim 44 , wherein the substrate is a heat-sensitive substrate selected from the group consisting of wood and plastic.