Ink composition for use on non-absorbent surfaces
View Patent ↗According to one aspect, an ink composition includes a colorant, one or more polymers such as a polyurethane siloxane, a surfactant, water, and a solvent. The ink composition has a total solids content of less than about 20% by weight. Further the ink has an initial surface tension of less than about 50 dynes per centimeter on application and the surface tension on drying should not increase by more than 20 percent.
1. An aqueous ink comprising:
from about 3 to about 15% by weight of a first urethane silanol polymer and a second urethane silanol polymer;
from about 0.5 to about 12% by weight of one or more colorants;
from about 5 to about 35% by weight of ethylene glycol;
from about 0.03 to about 1.0% by weight of a pH modifier; and
water, wherein the aqueous ink has a viscosity from about 1 to about 20 mPa-s such that the aqueous ink can be applied to a non-absorbent surface in a layer, and wherein the ink has a dynamic surface tension at 25 degrees Celsius from about 20 to about 45 dynes/cm, wherein the first urethane silanol polymer is polycarbonate based.
2. The aqueous ink of claim 1 , wherein the viscosity is from about 4 to about 14 mPa-s.
3. The aqueous ink of claim 1 , further comprising from about 0.1 to about 5% by weight of a surfactant.
4. An aqueous ink comprising:
from about 3 to about 15% by weight of a first urethane silanol polymer and a second urethane silanol polymer;
from about 0.5 to about 12% by weight of one or more colorants;
from about 5 to about 35% by weight of ethylene glycol;
from about 0.03 to about 1.0% by weight of a pH modifier; and
water, wherein the aqueous ink has a viscosity from about 1 to about 20 mPa-s such that the aqueous ink can be applied to a non-absorbent surface in a layer, and wherein the ink has a dynamic surface tension at 25 degrees Celsius from about 20 to about 45 dynes/cm, wherein the first urethane silanol polymer is polycarbonate based.
5. The aqueous ink of claim 4 , wherein the crosslinker is an iso-cyanate crosslinker.
6. The aqueous ink of claim 1 , wherein one of the one or more polymers is a self-crosslinking urethane silanol.
7. The aqueous ink of claim 1 , wherein the solvent is chosen from the group consisting of 1-(2-hydroxyethyl)-2-pyrrolidone, alcohols, polyols, glycerols, and glycols.
8. The aqueous ink of claim 4 , wherein the surfactant is an ethoxylated molecule.
9. A method for high speed variable printing comprising the steps of:
providing an aqueous ink, the aqueous ink comprising:
from about 3 to about 15% by weight of a first urethane silanol polymer and a second urethane silanol polymer, wherein the first urethane silanol polymer is polycarbonate based;
from about 0.5 to about 12% by weight of a pigment;
from about 5 to about 35% by weight of ethylene glycol;
from about 0.03 to about 1.0% by weight of a pH modifier; and
water, wherein the aqueous ink has a viscosity from about 1 to about 20 mPa-s, and wherein the ink has a dynamic surface tension at 25 degrees Celsius from about 20 to about 45 dynes/cm; and
applying the aqueous ink onto a non-absorbent substrate in a first layer.
10. The method of claim 9 , the method further comprising the step of applying the aqueous ink in a plurality of further layers.
11. The method of claim 9 , wherein the aqueous ink further comprises from about 0.1 to about 5.0% by weight of a surfactant.
12. The method of claim 9 , the method further comprising the step of applying heat to crosslink the one or more polymers of the aqueous ink.