View Patent ↗The present invention relates to a method of preparing purified carbon nanotubes (CNTs) comprising mixing starting CNTs with an organic solvent in the presence of sonication; substantially removing the organic solvent to obtain a CNT composition; and heating the CNT composition at 200° C. or higher to obtain the purified carbon nanotubes. The present invention further relates to the purified CNTs and cohesive CNT assemblies prepared from the method described herein, and articles (e.g. capacitor, energy storage device or capacitive deionization device) comprising the purified CNTs.
1. Purified carbon nanotubes having a Raman G/D ratio of at least 50 and a BET specific surface area of about 1200 m 2 /g or higher.
2. The purified carbon nanotubes according to claim 1 , having a Raman G/D ratio of at least 80.
3. The purified carbon nanotubes according to claim 1 , prepared by a method comprising the steps of:
(a) mixing starting carbon nanotubes with an organic solvent in the presence of sonication to produce a dispersion;
(b) substantially removing the organic solvent to obtain a carbon nanotube composition; and
(d) heating the carbon nanotube composition at 200° C. or higher in an atmosphere comprising between about 1 ppm to 10,000 ppm of oxygen;
wherein the organic solvent is selected from the group consisting of toluene, o-dichlorobenzene, isopropyl alcohol, N,N-dimethylformamide, substituted or unsubstituted benzene, chlorobenzene, m-dichlorobenzene, p-dichlorobenzene, trichlorobenzene, bromobenzene, m-dibromobenzene, o-dibromobenzene, p-dibromobenzene, tribromobenzene, toluene, o-xylene, m-xylene, p-xylene, 1,2-dichloroethane, 1,2-dibromoethane, chloroform, primary amines, secondary amines, tertiary amines, dimethyl sulfoxide, and any combinations thereof.
4. The purified carbon nanotubes according to claim 1 , in a form of a cohesive carbon assembly.