Purified carbon nanotubes and applications thereof
View Patent ↗The present invention relates to a method of preparing purified carbon nanotubes (CNTs) comprising mixing starting CNTs with an organic solvent in the presence of sonication; substantially removing the organic solvent to obtain a CNT composition; and heating the CNT composition at 200° C. or higher to obtain the purified carbon nanotubes. The present invention further relates to the purified CNTs and cohesive CNT assemblies prepared from the method described herein, and articles (e.g. capacitor, energy storage device or capacitive deionization device) comprising the purified CNTs.
1. An energy storage device comprising a current collector and an electrode on one side of an insulating material or an electrolyte, and another current collector and another electrode on the other side of the insulating material or the electrolyte, wherein at least one of the electrodes and/or at least one of the current collectors comprises purified carbon nanotubes having a Raman G/D ratio of at least 50 and a BET specific surface area of 1200 m 2 /g or higher.
2. The energy storage device according to claim 1 , wherein the purified carbon nanotubes have a Raman G/D ratio of at least 80.
3. The energy storage device according to claim 1 , wherein the purified carbon nanotubes are prepared by a method comprising the steps of:
(a) mixing starting carbon nanotubes with an organic solvent in the presence of sonication to produce a dispersion;
(b) substantially removing the organic solvent to obtain a carbon nanotube composition; and
(d) heating the carbon nanotube composition at 200° C. or higher in an atmosphere comprising between about 1 ppm to 10,000 ppm of oxygen;
wherein the organic solvent is selected from the group consisting of toluene, o-dichlorobenzene, isopropyl alcohol, N,N-dimethylformamide, substituted or unsubstituted benzene, chlorobenzene, m-dichlorobenzene, p-dichlorobenzene, trichlorobenzene, bromobenzene, m-dibromobenzene, o-dibromobenzene, p-dibromobenzene, tribromobenzene, o-xylene, m-xylene, p-xylene, 1,2-dichloroethane, 1,2-dibromoethane, chloroform, primary amines, secondary amines, tertiary amines, dimethyl sulfoxide, and any combinations thereof.
4. A capacitive deionization device comprising a current collector and an electrode on one side of a spacer, and another current collector and another electrode on the other side of the spacer, wherein at least one of the electrodes and/or at least one of the current collectors comprises purified carbon nanotubes having a Raman G/D ratio of at least 50 and a BET specific surface area of 1200 m 2 /g or higher.
5. The capacitive deionization device according to claim 4 , wherein the purified carbon nanotubes have a Raman G/D ratio of at least 80.
6. The capacitive deionization device according to claim 4 , wherein the purified carbon nanotubes are prepared by a method comprising the steps of:
(a) mixing starting carbon nanotubes with an organic solvent in the presence of sonication to produce a dispersion;
(b) substantially removing the organic solvent to obtain a carbon nanotube composition; and
(d) heating the carbon nanotube composition at 200° C. or higher in an atmosphere comprising between about 1 ppm to 10,000 ppm of oxygen;
wherein the organic solvent is selected from the group consisting of toluene, o-dichlorobenzene, isopropyl alcohol, N,N-dimethylformamide, substituted or unsubstituted benzene, chlorobenzene, m-dichlorobenzene, p-dichlorobenzene, trichlorobenzene, bromobenzene, m-dibromobenzene, o-dibromobenzene, p-dibromobenzene, tribromobenzene, o-xylene, m-xylene, p-xylene, 1,2-dichloroethane, 1,2-dibromoethane, chloroform, primary amines, secondary amines, tertiary amines, dimethyl sulfoxide, and any combinations thereof.
7. An electrochemical double-layer capacitor (EDLC) comprising two electrodes, an electrolyte, and a separator, wherein at least one electrode comprises purified carbon nanotubes having a Raman G/D ratio of at least 50 and a BET specific surface area of 1200 m 2 /g or higher,
for which a measured specific capacitance is greater than 50 Farad/gram, and a −45° complex impedance phase angle frequency is greater than 5 Hz.
8. The EDLC according to claim 7 , wherein the purified carbon nanotubes have a Raman G/D ratio of at least 80.
9. The energy storage device according to claim 1 , wherein the purified carbon nanotubes are in a form of a cohesive carbon assembly.
10. The capacitive deionization device according to claim 4 , wherein the purified carbon nanotubes are in a form of a cohesive carbon assembly.
11. The EDLC according to claim 7 , wherein the purified carbon nanotubes are in a form of a cohesive carbon assembly.
12. The EDLC according to claim 7 , wherein the purified carbon nanotubes are prepared by a method comprising the steps of:
(a) mixing starting carbon nanotubes with an organic solvent in the presence of sonication to produce a dispersion;
(b) substantially removing the organic solvent to obtain a carbon nanotube composition; and
(d) heating the carbon nanotube composition at 200° C. or higher in an atmosphere comprising between about 1 ppm to 10,000 ppm of oxygen;
wherein the organic solvent is selected from the group consisting of toluene, o-dichlorobenzene, isopropyl alcohol, N,N-dimethylformamide, substituted or unsubstituted benzene, chlorobenzene, m-dichlorobenzene, p-dichlorobenzene, trichlorobenzene, bromobenzene, m-dibromobenzene, o-dibromobenzene, p-dibromobenzene, tribromobenzene, o-xylene, m-xylene, p-xylene, 1,2-dichloroethane, 1,2-dibromoethane, chloroform, primary amines, secondary amines, tertiary amines, dimethyl sulfoxide, and any combinations thereof.