Super absorbent polymer and preparation method thereof
The present invention relates to a super absorbent polymer and a preparation method thereof. The super absorbent polymer includes surface crosslinked polymer particles prepared by surface crosslinking of particles of a base resin, wherein the base resin is polymerized from a monomer composition including water-soluble ethylene-based unsaturated monomers, and a water-soluble component, wherein the water-soluble component has a ratio (dwt/d(log M)) of 0.9 or less over molecular weights (M) ranging from 100,000 to 300,000 when measured from an eluted solution after swelling the super absorbent polymer for 1 hour, and wherein the content of the water-soluble component is 5% by weight or less, based on the total weight of the super absorbent polymer, when measured after swelling the super absorbent polymer for 1 hour. The super absorbent polymer has excellent liquid permeability even when swollen without a reduction in centrifuge retention capacity or absorbency under load while having improved permeability.
1. A super absorbent polymer, comprising:
surface crosslinked polymer particles prepared by surface crosslinking of particles of a base resin, wherein the base resin is polymerized from a monomer composition including water-soluble ethylene-based unsaturated monomers; and
a water-soluble component, wherein the water-soluble component has a ratio (dwt/d(log M)) of 0.9 or less over molecular weights (M) ranging from 100,000 to 300,000 when measured from an eluted solution after swelling 1 g of the super absorbent polymer in 200 ml of 0.9% NaCl solution at 25° C. for 1 hour, and
wherein the content of the water-soluble component is 2.5 to 5% by weight, based on the total weight of the super absorbent polymer, when measured after swelling the super absorbent polymer for 1 hour.
2. The super absorbent polymer of claim 1 , wherein the super absorbent polymer has centrifuge retention capacity ranging from about 26 to about 37g/g.
3. The super absorbent polymer of claim 1 , wherein the super absorbent polymer has an absorbency under load (0.7psi AUL) ranging from about 20 to about 26 g/g.
4. The super absorbent polymer of claim 1 , wherein the base resin is polymerized in the presence of an internal cross linking agent, which crosslinks polymers present in the interior of the polymer particles.
5. The super absorbent polymer of claim 4 , wherein the internal cross linking agent is present in an amount ranging from 0.1 to 0.5 wt % based on the monomer composition.
6. A hygiene product including the super absorbent polymer of claim 1 .
7. A disposable diaper including the super absorbent polymer of claim 1 .