ACCELERATOR SYSTEM, A COMPOSITION COMPRISING A SYNTHETIC ISOPRENE POLYMER AND THE ACCELERATOR SYSTEM, AND DIPPED GOODS MADE FROM THE COMPOSITION
This invention relates to an accelerator system comprising a sulphur donor, a carbamate or combination of carbamates as the only accelerator and optionally sulphur and optionally an activator, characterized in that the carbamate is a zinc dihydrocarbyldithiocarbamate, or a combination of zinc dihydrocarbyldithiocarbamates; a composition comprising a synthetic isoprene polymer latex and the accelerator system, and dipped goods made therefrom.
1 . A composition comprising: (a) a synthetic isoprene polymer; and (b) an accelerator system with respect to 100 parts by weight of the synthetic isoprene polymer wherein the composition comprises:
0.5 to 10 phr of a thiuram as sulphur donor:
0.05 to 2.0 phr of a carbamate or combination of carbamates as the only accelerator and
optionally at most 5.0 phr sulphur and
optionally at most 2.5 phr of an activator, characterized in that the carbamate is a zinc dihydrocarbyldithiocarbamate, or a combination of zinc dihydrocarbyldithiocarbamates.
2 . The composition according to claim 1 , wherein the hydrocarbyl groups independently may be alkyl or (substituted) aryl groups, preferably wherein the aryl group(s) (independently) have 6 to 12 carbon atoms and/or preferably wherein the alkyl group(s) (independently) have 1 to 6 carbon atoms.
3 . The composition according to claim 1 , wherein the carbamate is a zinc dialkyldithiocarbamate, preferably zinc dibutyldithiocarbamate (ZDBC) or zinc diethyldithiocarbamate (ZDEC), or a combination of ZDBC and ZDEC.
4 . A good comprising a composition a comprising synthetic isoprene polymer latex and an accelerator system, comprising 0.5 to 10 phr of a thiuram as sulphur donor, 0.05 to 2.0 phr of a carbamate as the only accelerator and optionally at most 5.0 phr sulphur and optionally at most 2.5 phr of an activator, wherein the carbamate is a zinc dihydrocarbyldithiocarbamate, or a combination of zinc dihydrocarbyldithiocarbamates.
5 . The good according to claim 4 , wherein the amount of carbamate is in the range of 0.05 to 2.0 phr.
6 . The good according to claim 4 , wherein the synthetic isoprene polymer latex is a polyisoprene latex.
7 . The good according to any one of claim 4 , containing no or less than 0.5 phr zinc oxide.
8 . The good of claim 4 , wherein the good is a dipped good obtainable by dipping a mould into the composition.