Glass fillers for composites
View Patent ↗The invention relates to a particulate glass filler wherein glass particles of 0.2 to 1 μm mean particle size are connected with other particles, the connection being effected by the glass material itself. More precisely particulate glass filler comprising glass particles, wherein the particles contains centrally located macro glass particles and on the outer surface located micro glass particles wherein the macro and micro glass particles are connected by the material of said particles. Further the invention relates to a method for manufacturing the glass particles and the particulate glass filler comprising said glass particles. It also relates to a composite or dental material comprising the above particulate glass filler.
1. A particulate glass filler comprising glass particles, wherein
the glass particles comprise centrally located macro glass particles with connections to micro glass particles located on an outer surface of the macro glass particles,
wherein the connections consist of a material of said glass particles,
wherein the glass particles have a refractive index n in the range of n=1.50 to 1.60, and
wherein the macro glass particles have a size in the range of 200 to 600 nm.
2. The particulate glass filler according to claim 1 , wherein the connections consist of a material of the macro glass particles.
3. The particulate glass filler according to claim 1 , wherein the macro glass particles are selected from dental glasses comprising barium and/or strontium.
4. The particulate glass filler according to claim 1 , wherein the macro glass particles are selected from dental glasses having a transition temperature lower than 650° C.
5. The particulate glass filler according to claim 1 , wherein the macro glass particles have a refractive index n in the range of n=1.50 to 1.58.
6. The particulate glass filler according to claim 1 , wherein the macro glass particles are selected from dental glasses comprising barium aluminum silicate glass and/or strontium aluminum silicate glass.
7. The particulate glass filler according to claim 1 , wherein the micro glass particles have a refractive index in the range of n=1.52 to 1.59.
8. The particulate glass filler according to claim 1 , wherein the micro glass particles are selected from dental glass ceramics having a transition temperature of greater than 700° C.
9. The particulate glass filler according to claim 1 , wherein the micro glass particles have a size in the range of 100 to 300 nm.
10. The particulate glass filler according to claim 1 , wherein the glass particles have a mean particle size in the range of 0.2 to 1.0 λm.
11. The particulate glass filler according claim 1 , wherein the particulate glass filler is amorphous.
12. A method of producing a particulate glass filler according to claim 1 comprising the following steps:
I. Dispersing glass filler with a refractive index n=1.50 to 1.60 with a suitable solvent;
II. Sintering and welding the dispersed glass filler at 450° C. to 800° C.;
III. Cooling the sintered glass filler to room temperature;
IV. Dispersing welded filler in a suitable solvent;
V. Drying of said glass filler; and
VI. Obtaining a particulate glass filler comprising glass particles.
13. The particulate glass filler according to claim 1 , wherein the macro glass particles have a size in the range of 400 nm±100 nm.
14. The particulate glass filler according to claim 1 , wherein the macro glass particles have a size in the range of 400 nm±50 nm.
15. The particulate glass filler according to claim 8 , wherein the micro glass particles are selected from dental glass ceramics having a transition temperature of greater than 750° C.
16. The particulate glass filler according to claim 8 , wherein the micro glass particles are selected from dental glass ceramics having a transition temperature of greater than 800° C.
17. The particulate glass filler according to claim 9 , wherein the micro glass particles have a size in the range of 200±5 nm.
18. The particulate glass filler according to claim 9 , wherein the micro glass particles have a size in the range of 180±5 nm.
19. The particulate glass filler according to claim 10 , wherein the glass particles have a mean particle size in the range of 0.3 to 0.6 μm.
20. The particulate glass filler according to claim 1 , wherein both the macro glass particles and the micro glass particles have a refractive index n in the range of n=1.50 to 1.60.