BLOCK PRODUCTS INCORPORATING SMALL PARTICLE THERMOPLASTIC BINDERS AND METHODS OF MAKING SAME
A block product comprising a thermoplastic binder having an average particle size of less than 20 micrometers fused with active particles to form a generally coherent porous structure. In some cases, the average particle size of the binder is less than 12 micrometers. In some cases, the active particles are activated carbon particles. In some cases, the block product may include one or more of poly(vinylidene difluoride) binders, nylon-11, and nylon-12 or other odd-numbered polyamides having such small particle size.
1 . A block product comprising a thermoplastic binder having an average particle size of less than 12 micrometers fused with active particles to form a generally coherent porous structure.
2 . The block product of claim 1 , wherein the average particle size of the binder is about 5 micrometers.
3 . The block product of claim 1 wherein the active particles are activated carbon particles.
4 . The block product of claim 1 , wherein the thermoplastic binder is selected from the group consisting of:
a) poly(vinylidene difluoride) binders;
b) nylon-11;
c) nylon-12; and
d) other odd-numbered polyamides
5 . A carbon block comprising a poly(vinylidene difluoride) binder fused with activated carbon.
6 . The carbon block of claim 5 wherein the binder has an average particle size of less than 20 micrometers.
7 . The carbon block of claim 5 , wherein the poly(vinylidene difluoride) binder comprises between about 5 and 14 percent of the carbon block by weight.
8 . The carbon block of claim 5 , wherein the average particle size of the binder is less than 12 micrometers.
9 . The carbon block of claim 5 , wherein the average particle size of the binder is about 5 micrometers.
10 . A method of making a carbon block comprising:
mixing a poly(vinylidene difluoride) binder powder with an activated carbon powder;
heating the mixture of binder and activated carbon powder;
compressing the mixture of binder and activated carbon powder.
11 . The method of claim 10 , wherein the poly(vinylidene difluoride) binder powder has an average particle size of less than 20 micrometers.
12 . The method of claim 10 , wherein the poly(vinylidene difluoride) binder powder has an average particle size of less than 12 micrometers.
13 . The method of claim 10 wherein the compression of the mixture is performed by compression transfer molding the mixture.
14 . The method of claim 10 , wherein the compression of the mixture is performed by extruding the mixture.
15 . A carbon block made by the method of claim 10 .
16 . A fluid filter comprising a carbon block according to claim 10 .