Insulating composite materials comprising an inorganic aerogel and a melamine foam
The invention relates to insulating composite materials comprising an inorganic aerogel and a melamine foam. The invention also relates to the production method of said materials, and to the use of same.
1. A composite comprising an inorganic aerogel reinforced by an open-cell melamine foam, wherein
said composite has a thermal conductivity λ between 10 and 20 mW/m-K measured using a guarded hot plate according to NF EN 12667 at 20° C. and atmospheric pressure,
a percentage of a volume occupied by macropores, macropores being pores with a diameter greater than 10 μm, in a volume occupied by the composite in its entirety is less than 5%,
the inorganic aerogel is non-granular, and
the inorganic aerogel has a continuous three-dimensional porous structure.
2. Composite according to claim 1 , produced by a process comprising the following successive steps: a) casting an inorganic sol in a reactor in which was previously placed the open-cell melamine foam, b) gelation of the sol into a lyogel, c) drying the lyogel.
3. Composite according to claim 1 , wherein the aerogel is formed from an inorganic sol comprising between 5% and 15% by weight of inorganic material based on the total weight of the inorganic sol.
4. Composite according to claim 1 , wherein macropores whose diameter is between 50 and 250 microns comprises more than 80% of total number of macropores of said composite.
5. Composite according to claim 1 , wherein the composite has a thickness of between 2 and 50 nm.
6. Composite g to claim 1 , wherein the composite has a density between 70 kg/m 3 and 150 kg/m 3 .
7. Composite according to claim 1 , wherein the melamine foam is a melamine-formaldehyde foam having a thickness of between 2 and 50 mm, a porosity of between 95% and 99.5%, a density between 8.5 and 11.5 kg/m3, and a thermal conductivity of between 35 and 40 mW/m-K measured using a guarded hot plate according to NF EN 12667 at 20° C. and atmospheric pressure.
8. Composite according to claim 1 , wherein the inorganic aerogel comprises silica, titanium oxide, manganese oxide, calcium oxide, carbonate calcium, zirconium oxide, or mixtures thereof.
9. Composite according to claim 1 , wherein the composite does not contain any binder.
10. Composite according to claim 9 , wherein the composite does not comprise a fibrous reinforcing material.
11. Composite according to claim 1 , wherein the composite has a quantity of residual solvent by weight of the composite of less than or equal to 3% according to EN/ISO 3251.
12. Composite according to claim 1 , wherein the aerogel further comprises an opacifier.
13. A sandwich panel comprising at least one layer consisting essentially of a monolithic composite according to claim 1 .
14. A multilayer thermal insulation panel comprising at least one layer of a composite according to claim 1 .
15. Acoustic insulation comprising at least one layer of a composite according to claim 1 .
16. Composite according to claim 1 , wherein composite has a thermal conductivity λ between 12.5 and 20 mW/m-K at 20° C. and atmospheric pressure.
17. Composite according to claim 1 , wherein less than 5% of the volume occupied by the composite is occupied by pores with a diameter greater than 5 μm.
18. Composite according to claim 1 , wherein the inorganic aerogel is in the form of a single block piece.