Abrasion-resistant steel material excellent in fatigue characteristics and method for manufacturing same
An abrasion-resistant steel material excellent in fatigue characteristics having a composition (in mass %) comprising 0.30 to 0.90% of C, 0.05 to 1.00% of Si, 0.10 to 1.50% of Mn, 0.003 to 0.030% of P, 0.001 to 0.020% of S, from 0.10 to 0.70% of Nb, and containing depending on necessity one or more of 1.50% or less of Cr, 0.50% or less of Mo, 0.50% or less of V, 2.00% or less of Ni, 0.10% or less of Ti, and 0.0050% or less of B, the balance Fe and unavoidable impurities, a metallic structure after a temper heat treatment having a Nb-containing carbide dispersed therein, the Nb-containing carbide particles having a particle diameter of 1.0 mm or more that is controlled to 200 particles per mm 2 or more, and a maximum particle diameter Dmax of Nb-containing carbide particles in 10 3 mm 3 that is controlled to 18.0 mm or less.
1. An abrasion-resistant steel material excellent in fatigue characteristics having a chemical composition comprising from 0.30 to 0.90% of C, from 0.05 to 1.00% of Si, from 0.10 to 1.50% of Mn, from 0.003 to 0.030% of P, from 0.001 to 0.020% of S, and from 0.10 to 0.70% of Nb, all in terms of percentage by mass, with the balance of Fe and unavoidable impurities; having a metallic structure after a temper heat treatment having a Nb-containing carbide dispersed therein; and having a number of Nb-containing carbide particles having a particle diameter of 1.0 μm or more that is controlled to 200 particles per mm 2 or more, and a maximum particle diameter Dmax of Nb-containing carbide particles in 10 3 mm 3 estimated by an extreme value statistics method that is controlled to 18.0 μm or less, assuming that a square root of an area of each of Nb-containing carbide particles found by observing a cross sectional structure is designated as the particle diameter of the particle.
2. The abrasion-resistant steel material excellent in fatigue characteristics according to claim 1 , wherein the abrasion-resistant steel material has the chemical composition further containing one or more kind of 1.50% or less of Cr, 0.50% or less of Mo, 0.50% or less of V, 2.00% or less of Ni, 0.10% or less of Ti, and 0.0050% or less of B.
3. A method for manufacturing an abrasion-resistant steel material according to claim 1 excellent in fatigue characteristics, comprising providing an abrasion-resistant steel material having been finally subjected to a temper heat treatment from a steel material having been subjected to casting and a cast material heat treatment, in which a heating temperature T (° C.) in the cast material heat treatment is determined corresponding to a C content and a Nb-content in the steel in such a manner that a G value determined by the following expression (1) is 0.53 or more, and a casting condition is controlled in such a manner that an average cooling rate (° C. per minute) from 1,500° C. to 1,000° C. in a center portion of the cast material on casting is the G value or more:
G value=0.39 exp(3.94 x ) (1)
wherein
x=Nb−10 y /C
y=3.42−7,900/(T+273)
C represents the C content (% by mass) in the steel, Nb represents the Nb content (% by mass) in the steel, and T represents the heating temperature (° C.) in the cast material heat treatment.