Process for the production of a microfibrillated cellulose composition
The present invention relates to a process for the production of microfibrillated cellulose composition, wherein the microfibrillated cellulose has an average fiber length in the range from 500 to 1300 μm and a percentage of fiber length in the category ≤200 μm of at least 15%, obtained by subjecting an aqueous mixture comprising 30 to 70% by weight of cellulose containing fibers to mechanical shearing at a temperature in the range of from ≥40° C. to ≤120° C. in the presence of at least one thermostable biocide, to the microfibrillated cellulose composition obtained in this process and their use in a process for production of paper, card and board comprising draining a paper stock comprising the microfibrillated cellulose composition with sheet formation in the wire.
1. A process for the production of a microfibrillated cellulose composition, the process comprising:
subjecting an aqueous mixture comprising 30 to 70% by weight of cellulose containing fibers to mechanical shearing at a temperature of from 40° C. to 120° C. in the presence of at least one thermostable biocide thereby forming the microfibrillated cellulose,
wherein the microfibrillated cellulose in the composition has an average fiber length of from 500 to 1300 μm and a percentage of a fiber in the composition having a length of 200 μm or less is at least 15%, and
wherein the thermostable biocide is a combination of octylisothiazolinone, glutaraldehyde, and sodium pyrithione.
2. The process according to claim 1 , wherein the cellulose containing fibers are bleached chemical pulp and/or wastepaper.
3. The process according to claims 1 , wherein the cellulose containing fibers are mechanically sheared in a single screw, twin screw or conical extruder or with a refiner.
4. The process according to claim 1 , wherein the microfibrillated cellulose has a freeness of at least 60 SR.
5. The process according to claim 1 , wherein the microfibrillated cellulose has a BET surface area of from 20 to 100 m 2 /g.
6. The process according to claim 1 , wherein the mechanical shearing is performed with an energy input of from 0.3 to 10 MWh/t of dry fiber.
7. The process according to claim 1 , wherein the cellulose containing fibers, which are virgin fibers, are a starting material for the microfibrillated cellulose.
8. The process according to claim 1 wherein the octylisothiazolinone is utilized in an amount of 185 parts per million on a weight by weight basis, the glutaraldehyde is utilized in an amount of 460 parts per million on a weight by weight basis, and the sodium pyrithione is utilized in an amount of 200 parts per million on a weight by weight basis.
9. The process according to claim 8 , wherein the cellulose containing fibers are derived from linerboard from recycled paper and/or old corrugated carton.
10. The process according to claim 1 , wherein the cellulose containing fibers are derived from linerboard from recycled paper and/or old corrugated carton.
11. A process for the production of a microfibrillated cellulose composition, the process comprising:
subjecting an aqueous mixture comprising 30 to 70% by weight of cellulose containing fibers to mechanical shearing at a temperature of from 40° C. to 120° C. in the presence of at least one thermostable biocide thereby forming the microfibrillated cellulose,
wherein the microfibrillated cellulose in the composition has a weight-weight averaged fiber length of 800 μm determined according to Tappi standard T 271 and a percentage of a fiber in the composition having a length of 200 μm or less is about 19%, and
wherein the thermostable biocide is a combination of octylisothiazolinone, glutaraldehyde, and sodium pyrithione,
wherein the octylisothiazolinone is utilized in an amount of 185 parts per million on a weight by weight basis, the glutaraldehyde is utilized in an amount of 460 parts per million on a weight by weight basis, and the sodium pyrithione is utilized in an amount of 200 parts per million on a weight by weight basis,
wherein the thermostable biocide is added during the step of mechanical shearing, and
wherein the cellulose containing fibers are derived from linerboard from recycled paper and/or old corrugated carton.
12. The process according to claim 11 wherein the thermostable biocide is added only during the step of mechanical shearing.