Flexible fire-retardant thermoplastic compositions having high thermomechanical strength, in particular for electric cables
A halogen-free fire-retardant thermoplastic composition composed of: 50% to 70% by weight of fire-retardant fillers, 0.1% to 45% by weight of a copolymer of ethylene and of an ethylenic monomer bearing a polar function, 10% to 25% by weight of a non-functionalized very low density polyethylene (VLDPE), optionally, up to 10% of additives, and 0.1% to 10% by weight of a linear low density polyethylene (LLDPE), characterized in that the density of the very low density polyethylene (VLDPE) is between 0.85 and 0.91, in that the density of the linear low density polyethylene is greater than 0.91 and in that the linear low density polyethylene (LLDPE) is grafted with maleic anhydride grafts present on the main chain. Also, a cable, tube, pipe or the like, a layer of which is formed with said composition.
1. A halogen-free fire-retardant thermoplastic composition consisting of:
50% to 75% by weight of fire-retardant filler, wherein the fire-retardant filler is one or more selected from the group consisting of aluminum trihydroxide and magnesium dihydroxide;
0.1% to 45% by weight of a copolymer consisting of ethylene and vinyl esters of saturated carboxylic acid monomers;
only one non-functionalized very-low-density polyethylene (VLDPE) having a density between 0.85 and 0.91, present in an amount of 10% to 25% by weight;
0.1% to 10% by weight of a linear low-density polyethylene (LLDPE) having a density greater than 0.91, wherein the LLDPE is grafted with maleic anhydride grafts present on its main chain,
optionally up to 10% by weight of additives,
wherein the additives are chosen from antioxidants, UV stabilizers, antistatic agents, inorganic fillers, coloring pigments, zeolites, anti-dripping agents and/or plasticizers,
wherein the composition has following characteristics:
elongation at break is ≥200%, measured according to the standard ISO R527; and
breaking stress of the composition is ≥10 MPa, measured according to the standard ISO R527.
2. The composition of claim 1 , wherein the linear low-density polyethylene (LLDPE) is between 2.5% and 7% by weight of the composition.
3. The composition of claim 1 , wherein the non-functionalized very-low-density polyethylene (VLDPE) represents at most 20% by weight of the composition.
4. The composition of claim 1 , wherein the vinyl esters of saturated carboxylic acid comprises from 3 to 20 carbon atoms.
5. The composition of claim 1 , wherein the fire-retardant fillers represent more than 60% by weight of the composition.
6. A cable or pipe comprising at least two layers, at least one layer of which is formed by the thermoplastic composition of claim 1 .
7. The composition of claim 1 , wherein the anti-dripping agents are based on a silicone or fluorinated product.
8. A halogen-free fire-retardant thermoplastic composition consisting of:
50% to 75% by weight of fire-retardant filler, wherein the fire-retardant filler is one or more selected from the group consisting of aluminum trihydroxide and magnesium dihydroxide;
0.1% to 45% by weight of a copolymer consisting of ethylene and vinyl esters of saturated carboxylic acid monomers;
only one non-functionalized very-low-density polyethylene (VLDPE) having a density between 0.85 and 0.91, present in an amount of 10% to 25% by weight;
0.1% to 10% by weight of a linear low-density polyethylene (LLDPE) having a density greater than 0.91, wherein the LLDPE is grafted with maleic anhydride grafts present on its main chain, and
wherein the composition has following characteristics:
elongation at break is ≥200%, measured according to the standard ISO R527; and
breaking stress of the composition is ≥10 MPa, measured according to the standard ISO R527.