Diene elastomer modified by coupling having silanol functions, synthesis method for same, and rubber composition comprising modified diene elastomer
View Patent ↗The present invention relates to a modified diene elastomer predominantly comprising a species coupled via a group bearing a function comprising a silicon atom predominantly hydrolyzed into silanol and a tertiary amine function, linked to the diene elastomer via the silicon atom, and to the process for synthesizing the modified diene elastomer. This elastomer has the particular feature of not undergoing any change in Mooney viscosity during its storage.
1. A modified diene elastomer comprising a species represented by formula (1)
in which:
the symbol E denotes a diene elastomer,
R is a linear or branched C 1 -C 10 alkylene, C 6 -C 18 arylene or C 7 -C 18 aralkylene divalent hydrocarbon-based group,
R 1 and R 2 , which may be identical or different, represent a C 1 -C 18 alkyl radical, or else R 1 and R 2 form, with N to which they are attached, a heterocycle,
—OR″ represents an alkoxy function, hydrolysed to at least 50%, the alkyl radical in the alkoxy function comprising 1 to 5 carbon atoms.
2. The modified diene elastomer according to claim 1 , wherein the coupled species of the elastomer is represented by formula (1b)
in which:
the symbol E denotes a diene elastomer,
R is a linear or branched C 1 -C 10 alkylene, C 6 -C 18 arylene or C 7 -C 18 aralkylene divalent hydrocarbon-based group, R 1 and R 2 , which may be identical or different, represent a C 1 -C 18 alkyl radical, or else R 1 and R 2 form, with N to which they are attached, a heterocycle containing a nitrogen atom and at least one carbon atom.
3. The modified diene elastomer according to claim 1 , wherein in formula (I), R represents the linear C3 alkylene radical.
4. The modified diene elastomer according to claim 1 , wherein in formula (I), R 1 and R 2 , which may be identical or different, represent a methyl or ethyl radical.
5. The modified diene elastomer according to claim 1 , wherein the modified diene elastomer E is an SBR.
6. A process for synthesizing a modified diene elastomer, comprising the following steps:
anionic polymerization of at least one conjugated diene monomer in the presence of a polymerization initiator to obtain a living diene elastomer bearing an active site,
modification of the living diene elastomer bearing an active site obtained in the preceding step with a functionalization agent bearing at least one function that is hydrolysable into silanol and two functions that are reactive with the living elastomer, each directly linked to the silicon atom, and also a tertiary amine function, with a mole ratio of the functionalization agent to the polymerization initiator having a value ranging from 0.35 to 0.65 to obtain a modified elastomer,
hydrolysis of the modified elastomer obtained in the preceding step.
7. The process according to claim 6 , wherein the functionalization agent is a compound bearing —Si(OR) 3 , R being a hydrolysable C 1 -C 5 , and a tertiary amine function.
8. The process according to claim 6 , wherein the functionalization agent is a compound bearing —SiX 3 , X denoting a halogen, and a tertiary amine function.
9. The process according to claim 6 , wherein the functionalization agent is represented by formula 2:
in which:
R is a linear or branched C 1 -C 10 alkylene, C 6 -C 18 arylene or C 7 -C 18 aralkylene divalent hydrocarbon-based group,
R 1 and R 2 , which may be identical or different, represent a C 1 -C 18 alkyl radical, or else R 1 and R 2 form, with N to which they are attached, a heterocycle containing a nitrogen atom and at least one carbon atom,
the substituted or unsubstituted radicals R′, which may be identical to or different from each other, represent a C 1 -C 5 alkyl group.
10. The process according to claim 6 , wherein the hydrolysis step is performed by adding an aqueous hydrochloric acid solution.
11. A crosslinkable or crosslinked reinforced rubber composition based on at least one reinforcing filler and an elastomer matrix comprising at least one modified diene elastomer as defined in claim 1 .
12. The crosslinkable or crosslinked reinforced rubber composition according to claim 11 , wherein the reinforcing filler comprises a reinforcing mineral filler of siliceous type.
13. A tire tread comprising a crosslinkable or crosslinked rubber composition according to claim 11 .
14. A tire comprising a tread according to claim 13 .
15. The modified diene elastomer according to claim 1 , wherein the —OR″ represents an alkoxy function, hydrolysed to at least 80%, and the alkyl radical in the alkoxy function comprising 1 or 2 carbon atoms.
16. The modified diene elastomer according to claim 15 , wherein the “—OR” which represents an alkoxy function is hydrolysed to 100%.