Continuous casting method
In a continuous casting apparatus 100 for casting a stainless steel billet 3 c , a long nozzle 2 extending into a tundish 101 is provided at a ladle 1 for pouring a molten stainless steel 3 in the ladle 1 into the tundish 101 . Further, a nitrogen gas 4 is supplied as a seal gas around the molten stainless steel 3 in the tundish 101 , and continuous casting of the stainless steel billet 3 c is performed, in which, while immersing the spout 2 a of the long nozzle 2 into the molten stainless steel 3 in the tundish 101 , the molten stainless steel 3 is poured through the long nozzle 2 into the tundish 101 and the molten stainless steel 3 in the tundish 101 is poured into a casting mold 105.
1. A continuous casting method for casting a solid metal by pouring a molten metal in a ladle into a tundish disposed therebelow and continuously pouring the molten metal in the tundish into a casting mold, the continuous casting method comprising:
supplying a nitrogen gas as a seal gas around the molten metal in the tundish;
pouring into the tundish the molten metal in the ladle through a pouring nozzle so that the molten metal in the tundish immerses a spout of the pouring nozzle, which serves for pouring into the tundish the molten metal in the ladle; and
pouring into the casting mold the molten metal in the tundish, while the spout of the pouring nozzle is immersed by the molten metal in the tundish;
wherein a tundish powder is sprayed over a surface of the molten metal in the tundish after the step of supplying the nitrogen gas and before the step of pouring into the casting mold the molten metal in the tundish, and the tundish powder is interposed between the molten metal and the nitrogen gas, and wherein the tundish powder comprises a synthetic slag agent which absorbs the nitrogen component contained in the molten metal.
2. The continuous casting method of claim 1 , wherein the spout of the pouring nozzle is inserted to a depth of 100 mm to 150 mm into the molten metal in the tundish.
3. The continuous casting method of claim 2 , wherein the solid metal which is to be cast is a stainless steel with a concentration of contained nitrogen of 400 ppm or less.
4. The continuous casting method of claim 1 , wherein the solid metal which is to be cast is a stainless steel with a concentration of contained nitrogen of 400 ppm or less.
5. The continuous casting method of claim 1 further comprising adjusting the flow rate of the molten metal pouring into the tundish and the flow rate of the molten metal pouring into the casting mold so that a surface of the molten metal in the tundish is maintained at a predetermined depth in an interior of the tundish, wherein the spout of the pouring nozzle remains immersed by the molten metal in the tundish.