Coated plug wrap for a smoking article
The present invention is directed to a coated plug wrap for a smoking article. The coated plug wrap is comprised of a base paper and a coating. In accordance with the present disclosure, the base paper may be comprised of hardwood pulp fibers and optionally, softwood pulp fibers. The base paper may be coated with a coating material such as an acrylate, a styrene, a butadiene, a starch, a starch derivative, a cellulose derivative, an alginate, a polyvinyl alcohol, a polyvinyl acetate, a gelatin, a gum, or a combination thereof. In one embodiment, the coated plug wrap may be incorporated into a smoking article.
1. A coated plug wrap for a smoking article, the coated plug wrap comprising:
a base paper comprising hardwood pulp fibers and softwood pulp fibers, wherein the base paper comprises greater than 80% hardwood pulp fibers based on the total dry weight of the fibers; wherein the base paper without any coating applied has an initial permeability of about 20 Coresta units or less, wherein the coated plug wrap has a permeability of less than about 10 Coresta units;
a coating on at least one surface of the base paper, the coating comprising an acrylate, a styrene, a butadiene, a starch, a starch derivative, a cellulose derivative, an alginate, a polyvinyl alcohol, a polyvinyl acetate, a gelatin, a gum, or a combination thereof, wherein the coated plug wrap has a moisture content of less than about 10% by weight; and
wherein the coated plug wrap has a Kit rating of at least 4.
2. The coated plug wrap according to claim 1 , wherein the coating comprises an acrylate, a styrene, a butadiene, or a combination thereof.
3. The coated plug wrap according to claim 1 , wherein the hardwood pulp fibers comprise eucalyptus fibers.
4. The coated plug wrap according to claim 1 , wherein the base paper comprises calcium carbonate in an amount of less than about 10% by weight.
5. The coated plug wrap according to claim 1 , wherein the coating is present in an amount of greater than about 70% of the surface area of at least one surface of the base paper.
6. The coated plug wrap according to claim 1 , wherein the coated plug wrap has a thickness of from about 10 μm to about 35 μm and a basis weight of from about 10 gsm to about 50 gsm.
7. A smoking article comprising the coated plug wrap of claim 1 .
8. The coated plug wrap according to claim 1 , wherein the hardwood pulp fibers have an average fiber length of from about 0.1 mm to about 2 mm, wherein the softwood pulp fibers have an average fiber length of from about 5 mm to about 10 mm.
9. The coated plug wrap according to claim 1 , wherein the base paper comprises a mineral filler in an amount of less than about 15% by weight.
10. The coated plug wrap according to claim 1 , wherein the base paper comprises a wet strength agent.
11. The coated plug wrap according to claim 1 , wherein the coated plug wrap has a contact angle with water of about 45° or more.
12. The coated plug wrap according to claim 1 , wherein the coating has a thickness of greater than 0.5 μm and less than about 12 μm.