Foamed styrenic polymers containing a brominated styrene-butadiene copolymer and having enhanced cell size homogeneity
View Patent ↗Extruded polymer foams are made from a polymer composition that includes an unbrominated styrenic polymer, a brominated vinyl aromatic/butadiene flame retardant, and an unbrominated vinyl aromatic/butadiene polymer. The unbrominated vinyl aromatic/butadiene polymer improves the cell homogeneity.
1. A monolithic foamed polymer composition having a polymeric phase which contains gas-filled cells, wherein the polymer phase comprises:
(a) one or more thermoplastic, non-brominated styrenic polymers containing no more than 1% polymerized diene monomers,
(b) a thermoplastic brominated vinyl aromatic/butadiene copolymer having a molecular weight of at least 1000 g/mol in an amount sufficient to provide 0.25 to 5% by weight bromine based on the combined weights of components (a), (b) and (c), and
(c) from 0.1 to 5 parts by weight, per part by weight of component (b) of at least one thermoplastic unbrominated vinyl aromatic/butadiene block copolymer selected from the group consisting of a thermoplastic unbrominated styrene-butadiene-styrene triblock copolymer containing a central poly(butadiene) block of 30,000 to 100,000 g/mol and terminal polystyrene blocks each having a molecular weight of 20,000 to 100,000 g/mol and a thermoplastic unbrominated styrene-butadiene diblock copolymer in which the polystyrene block has a molecular weight of 30,000 to 75,000 g/mol and the poly(butadiene) block has a molecular weight of 40,000 to 100,000 g/mol.
2. The monolithic foamed polymer composition of claim 1 which is an extruded foam having a thickness in the direction of expansion of at least 12 mm.
3. The monolithic foamed polymer composition of claim 1 , wherein the thermoplastic unbrominated vinyl aromatic/butadiene block copolymer is the styrene-butadiene-styrene triblock copolymer containing a central poly(butadiene) block of 30,000 to 100,000 g/mol and terminal polystyrene blocks each having a molecular weight of 20,000 to 100,000 g/mol.
4. The monolithic foamed polymer composition of claim 1 , wherein the thermoplastic unbrominated styrene-butadiene-styrene triblock copolymer contains a central poly(butadiene) block of 40,000 to 75,000 g/mol molecular weight and terminal polystyrene blocks each having a molecular weight of 40,000 to 75,000 g/mol.
5. The monolithic foamed polymer composition of claim 1 , wherein the thermoplastic unbrominated vinyl aromatic/butadiene block copolymer is the styrene-butadiene diblock copolymer in which the polystyrene block has a molecular weight of 30,000 to 75,000 g/mol and the poly(butadiene) block has a molecular weight of 40,000 to 100,000 g/mol.
6. The monolithic foamed polymer composition of claim 1 , wherein the amount of component (b) is sufficient to provide at least 0.5 weight % bromine based on the combined weights of components (a), (b) and (c).
7. The monolithic foamed polymer composition of claim 1 , wherein component (a) is polystyrene, a copolymer of at least 70% weight percent styrene and up to 30 weight percent acrylonitrile, or a mixture thereof.
8. A process for preparing the monolithic foamed polymer composition of claim 1 , comprising
(I) forming a pressurized molten mixture of:
(a) one or more thermoplastic non-brominated styrenic polymers containing no more than 1% polymerized diene monomers,
(b) a brominated flame retardant having a molecular weight of at least 1000 g/mol in an amount sufficient to provide 0.25 to 5% by weight bromine based on the combined weights of components (a), (b) and (c),
(c) from 0.1 to 5 parts by weight per part by weight of component (b) of at least one thermoplastic unbrominated vinyl aromatic/butadiene block copolymer selected from the group consisting of a thermoplastic unbrominated styrene-butadiene-styrene triblock copolymer containing a central poly(butadiene) block of 30,000 to 100,000 g/mol and terminal polystyrene blocks each having a molecular weight of 20,000 to 100,000 g/mol and a thermoplastic unbrominated styrene-butadiene diblock copolymer in which the polystyrene block has a molecular weight of 30,000 to 75,000 g/mol and the poly(butadiene) block has a molecular weight of 40,000 to 100,000 g/mol, and
(d) at least one physical blowing agent, wherein the temperature of the molten mixture is greater than the boiling temperature of the physical blowing agent(s); and
(II) passing the pressurized molten mixture through an opening into a zone of reduced pressure such that the blowing agent expands and the polymer composition cools and hardens to form the foamed polymer composition.
9. The process of claim 8 wherein in step (II) the foamed polymer composition has a thickness of at least 12 mm in the direction of expansion.
10. The process of claim 8 wherein the amount of component (b) is sufficient to provide at least 0.5 weight % bromine based on the combined weights of components (a), (b) and (c).
11. The process of claim 8 wherein component (a) is polystyrene, a copolymer of at least 70% weight percent styrene and up to 30 weight percent acrylonitrile, or a mixture thereof.
12. The process of claim 8 wherein step (I) is performed in an extrusion apparatus equipped with an auxiliary cooling device.