Nitrile rubber article having natural rubber characteristics
View Patent ↗An carboxylated nitrile-butadiene rubber latex formulation composed of a blend of a first acrylonitrile terpolymer and a second acrylonitrile terpolymer, wherein: the acrylonitrile content of the blended terpolymers is between 17 and 45% by weight, the methacrylic acid content of the blended terpolymers is less than 15% by weight, and the remaining balance of the terpolymers being butadiene. The invention also includes an elastomeric nitrile rubber article made from the formulation.
1. A carboxylated nitrile-butadiene rubber latex formulation comprising a blend of a first acrylonitrile terpolymer and a second acrylonitrile terpolymer, wherein the first acrylonitrile terpolymer and the second acrylonitrile terpolymer are in a compositional ratio ranging from 60:40 to 40:60, wherein:
the blend has an acrylonitrile content between 17 and 45% by weight, and
the blend has a methacrylic acid content of less than 15% by weight,
wherein a remaining balance of the blend is butadiene.
2. The formulation of claim 1 , wherein the first acrylonitrile terpolymer has a lower modulus relative to the second acrylonitrile terpolymer.
3. The formulation of claim 1 , wherein the carboxylated nitrile-butadiene rubber latex formulation further comprises, in terms of parts per 100 dry parts of rubber consisting of the blend of the first acrylonitrile terpolymer and the second acrylonitrile terpolymer, between 0-1.5 parts of an alkali agent that provides monovalent ions and 0.5-1.5 parts of a metallic oxide wherein a total combined amount of the alkali agent and metallic oxide is greater than 1.0 part per 100 dry parts of rubber.
4. The formulation of claim 3 , further comprising in terms of parts per 100 dry parts of rubber consisting of the carboxylated nitrile-butadiene terpolymer, from 0.5-1.5 parts sulfur and 0.5-1.5 parts rubber accelerator.
5. The formulation of claim 1 , wherein the formulation has a pH of 9 to 12.5.
6. The formulation of claim 1 , wherein the formulation is an emulsion containing 15-25% total solids content.
7. The formulation of claim 1 , wherein the formulation has a polymer structure comprising a random terpolymer of acrylonitrile, butadiene and carboxylic acid.