THERMAL SHOCK RESISTANT COATED EXHAUST SENSOR
A sensor element includes a substrate ( 10 ) having a coating ( 31 ) on a portion of the substrate ( 10 ). The coating ( 31 ) is applied to the substrate ( 10 ) by dipping the portion of the substrate ( 10 ) into a slurry which includes a pulverized mineral and water, extracting the substrate ( 10 ) from the slurry in a direction along an axis, drying the coated substrate ( 10 ), and firing the coated substrate ( 10 ) so as to promote densification of the mineral and adhesion of the mineral to the substrate ( 10 ). The coating ( 31 ) after firing has a minimum thickness of about 100 microns at every location around the periphery of a cross section through the substrate ( 10 ) taken in a plane normal to the axis. A method for making a coated sensor element is also disclosed.
1 . A method for making a coated sensor element comprising the steps of:
dipping a portion of a fired sensor element into a slurry that comprises a pulverized mineral and water, extracting the sensor element from the slurry, drying the sensor element so as to leave the pulverized mineral deposited on the sensor element, firing the sensor element with the pulverized mineral deposited thereon using a time and temperature profile effective to sinter the pulverized mineral into a protective coating ( 31 ) so as to provide good cohesion of the protective coating ( 31 ) and good adhesion of the protective coating ( 31 ) to the sensor element while avoiding cracking in the sensor element and the protective coating ( 31 ).
2 . The method according to claim 10 , wherein the slurry further comprises a volatile solid material, said volatile solid material being vaporized when the coated sensor element is fired so as to result in controlled porosity in the coating ( 31 ).
3 . The method according to claim 11 , wherein the volatile solid material is selected from the group consisting of graphite, carbon black, starch, nylon, polystyrene, latex, other insoluble organics, and combinations of one or more of the foregoing fugitive materials.
4 . The method according to claim 10 , wherein the slurry further comprises a dispersant.
5 . The method according to claim 13 , wherein the dispersant comprises ammonium polymethacrylate.
6 . The method according to claim 10 , wherein the pulverized mineral comprises alumina.
7 . The method according to claim 10 , wherein an outer surface of the sensor element includes a porous protection layer ( 15 ) that abuts an edge ( 34 ) of a sensor protective layer ( 14 ), and wherein the sensor element is dipped into the slurry a sufficient amount such that the slurry covers the edge ( 34 ) where the porous protection layer ( 15 ) abuts the sensor protective layer ( 14 ).
8 . The method according to claim 16 , wherein the slurry extends axially a minimum of 1 mm. beyond the edge ( 34 ) where the porous protection layer ( 15 ) abuts the sensor protective layer ( 14 ).
9 . The method according to claim 10 , additionally comprising, after the extracting step and prior to the drying step, the steps of
partially drying the dipped sensor element,
dipping the partially dried sensor element into the slurry a second time,
extracting the sensor element from the slurry after the second dipping step.