View Patent ↗A method of producing an interbody spinal implant. The method includes the steps of obtaining a blank having a top surface, bottom surface, opposing lateral sides, and opposing anterior and posterior portions, and applying a subtractive process (e.g., masked acid etching) to the top surface, the bottom surface, or both surfaces of the blank to form a roughened surface topography. Subsequently, the blank is machined to form the interbody spinal implant, which includes a body having a top surface, a bottom surface, opposing lateral sides, opposing anterior and posterior portions, a substantially hollow center, and a single vertical aperture where the top surface, the bottom surface, or both surfaces of the interbody spinal implant have the roughened surface topography produced by the subtractive process. This simplified method produces more accurate and repeatable implants with fewer process steps and defects, reducing process time and costs.
1. A method of producing an interbody spinal implant, comprising
applying a subtractive process to at least one surface of a metal blank to form a roughened surface topography on the at least one surface, the surface topography comprising micro features having a maximum peak to valley height within the micrometer size scale and nano features having a maximum peak to valley height within the nanometer size scale; and
subsequently, machining the blank to form an interbody spinal implant including a body having a shape for implantation into an intervertebral disc space through the posterior, the anterior, a lateral side, or the foramen of the spine, having surface structures that preserve vertebral endplate bone, that provide stability of the implant in the intervertebral disc space, and that resist expulsion of the implant from the intervertebral disc space, and having at least one vertical aperture for graft containment.
2. The method of claim 1 further comprising applying a maskant to the blank before applying the subtractive process.
3. The method of claim 2 , wherein the maskant is applied via sputtering, deposition, or evaporation.
4. The method of claim 1 , wherein the roughened surface topography is oriented in opposition to the biologic forces on the interbody spinal implant and to the direction of implantation.
5. The method of claim 1 , wherein the roughened surface topography promotes bone growth.
6. The method of claim 1 , wherein the roughened surface topography further comprises a roughness average amplitude, Ra, of about 1 to 200 microns.
7. The method of claim 1 , where the subtractive process comprises abrasive blasting of the at least one surface.
8. The method of claim 7 , wherein the subtractive process further comprises chemical etching the at least one surface.
9. The method of claim 8 , wherein the chemical etching comprises mild acid etching.
10. The method of claim 1 , wherein the subtractive process comprises chemical etching of the at least one surface.
11. The method of claim 1 , wherein the machining includes milling, turning, or both milling and turning.
12. The method of claim 1 , further comprising machining the body to include a slope or angle.
13. The method of claim 1 , wherein the metal comprises titanium or a titanium alloy.
14. The method of claim 1 , further comprising machining the body to include smooth, rounded, or smooth and rounded sides or corners.