Puncture resistant material
View Patent ↗A puncture resistant material is made from high modulus continuous filament polypropylene yarns which are twisted and woven into a tight weave. Batting materials are placed adjacent the woven layer (which may comprise one or more individual woven layers) to form a stack and the stack is needlepunched to form a consolidated material. The material is heat treated and calendared and the finished product may be used in applications where puncture resistance is required, such as in a shoe insole material.
1. A flexible puncture-resistant material, comprising:
a woven layer comprised of tightly woven yarns made from twisted high modulus continuous filament polypropylene;
said woven layer having 1-10 oz/yd 2 thermoplastic batting fibers needlepunched in a perpendicular direction into the woven layer forming a consolidated material;
said consolidated material being (i) condensed by heat treatment at a temperature above a glass transition temperature of the thermoplastic batting fibers to partially melt but not completely melt the thermoplastic batting fibers, thereby thermally shrinking the thermoplastic fibers, and (ii) reduced in thickness by calendaring.
2. The material according to claim 1 , wherein the thermoplastic yarns are twisted at 1-5 turns per inch prior to weaving.
3. The material according to claim 1 , wherein the woven layer is a 20×20 to 30×30 plain weave.
4. The material according to claim 1 , wherein the woven layer is a plain weave with greater than about 90% cover factor.
5. The material according to claim 1 , wherein the woven layer comprises 1 to 20 individual woven layers.
6. The material according to claim 1 , wherein the batting fibers consist of about 1 to about 10 oz/yd 2 of a blend of thermoplastic fibers.
7. The material according to claim 1 , wherein the consolidated material has a density increased by about 5% to about 20% compared to the consolidated material prior to heat treatment.
8. The material according to claim 1 , wherein the consolidated material has a density increased by about 10 to 12% compared to the consolidated material prior to heat treatment.
9. The material according to claim 1 , having a thickness of about 0.10 to about 0.20 inches.
10. The material according to claim 1 , having a thickness of about 0.05 to about 0.50 inches.
11. The material according to claim 1 , meeting ASTM 2412/2413 for puncture resistance.
12. A shoe sole comprising an insole made of the puncture resistant material according to claim 1 .
13. The material according to claim 1 , wherein said thermoplastic batting material fibers are made of the same high modulus continuous filament polypropylene as the woven layer and the fibers of the woven layer are partially but not completely melted.