Covering material for electric wire and covered electric wire
A covering material for an electric wire contains a polyvinyl chloride. The covering material has a property of a change curve of loss modulus with respect to temperature which shows no peak within a temperature range in a usage environment for the electric wire.
1. A covering material for an electric wire, the covering material having a composition containing a polyvinyl chloride,
wherein the composition of the covering material comprises a characteristic such that a change curve of a loss modulus with respect to temperature for the composition of the covering material containing the polyvinyl chloride has no peak within a temperature range of −30° C. to 60° C., which is a temperature range in a usage environment for the electric wire, and
wherein the composition of the covering material comprises more than or equal to 35 parts by weight and less than or equal to 50 parts by weight of a plasticizer and 2 to 20 parts by weight of a flexible resin with a melt flow rate of 1.0 g/10 min or less, the plasticizer and the flexible resin combined with respect to 100 parts by weight of the polyvinyl chloride such that the composition comprises the characteristic.
2. The covering material for the electric wire according to claim 1 , wherein the polyvinyl chloride has a degree of polymerization of 1400 or more.
3. A covered electric wire comprising:
a covering material for an electric wire, the covering material having a composition containing a polyvinyl chloride, wherein the composition of the covering material comprises a characteristic such that a change curve of a loss modulus with respect to temperature for the composition of the covering material containing the polyvinyl chloride has no peak within a temperature range of −30° C. to 60° C., which is a temperature range in a usage environment for the electric wire, and wherein the composition of the covering material comprises more than or equal to 35 parts by weight and less than or equal to 50 parts by weight of a plasticizer and 2 to 20 parts by weight of a flexible resin with a melt flow rate of 1.0 g/10 min or less, the plasticizer and the flexible resin combined with respect to 100 parts by weight of the polyvinyl chloride such that the composition comprises the characteristic; and
a conductor covered with the covering material for the electric wire.