Ocular implant made by a double extrusion process
The invention provides biodegradable implants sized for implantation in an ocular region and methods for treating medical conditions of the eye. The implants are formed from a mixture of hydrophilic end and hydrophobic end PLGA, and deliver active agents into an ocular region without a high burst release.
1. A bioerodible implant for treating an ocular condition comprising particles of dexamethasone dispersed within a biodegradable polymer matrix, wherein
at least 75% of the particles of dexamethasone have a diameter of less than 20 μm,
the biodegradable polymer comprises a poly(lactic-co-glycolic)acid (PLGA) ester end copolymer and a poly(lactic-co-glycolic)acid (PLGA) acid end copolymer,
the ratio of lactic to glycolic acid monomers in the PLGA ester end copolymer and the PLGA acid end copolymer is 50/50 weight percentage, and
the bioerodible implant is prepared by milling the biodegradable polymer and subjecting the dexamethasone and the biodegradable polymer to a double extrusion process;
wherein the dexamethasone is 60% by weight of the bioerodible implant; and wherein the implant releases about 60% of the dexamethasone in 14 days in vitro.
2. The bioerodible implant of claim 1 , wherein at least 99% of the particles of the dexamethasone have a diameter of less than 20 μm.
3. The bioerodible implant of claim 1 , wherein the implant is sized for implantation in an ocular region.
4. The bioerodible implant of claim 3 , wherein the ocular region is selected from the group consisting of the anterior chamber, the posterior chamber, the vitreous cavity, the choroid, the suprachoroidal space, the conjunctiva, the subconjunctival space, the episcleral space, the intracorneal space, the epicorneal space, the sclera, the pars plana, surgically-induced avascular regions, the macula and the retina.
5. The bioerodible implant of claim 4 , wherein the ocular region is the vitreous cavity.
6. The bioerodible implant of claim 1 , wherein the PLGA ester end copolymer and the PLGA acid end copolymer together are 40% by weight of the bioerodible implant.
7. The bioerodible implant of claim 1 , wherein the ocular condition is selected from the group consisting of uveitis, macular edema, macular degeneration, retinal detachment, ocular tumors, fungal or viral infections, multifocal choroiditis, diabetic retinopathy, proliferative vitreoretinopathy (PVR), sympathetic ophthalmia, Vogt Koyanagi-Harada (VKH) syndrome, histoplasmosis, uveal diffusion, and vascular occlusion.
8. The bioerodible implant of claim 7 , wherein the ocular condition is selected from the group consisting of uveitis, macular edema, vascular occlusive conditions, proliferative vitreoretinopathy (PVR), and other retinopathies.