Urethane Coating Composition For Metal Substrate
A urethane composition useful in a variety of applications such as, for example, as a direct-to-metal coating, i.e. a coating composition that can be applied directly to the surface of a metal substrate without a primer or pretreatment is described. The coating composition preferably includes a polyol that is the reaction product of a resin of general formula (I) with an acid or a diol respectively, with the reaction being carried out in the presence of a catalyst. The coating composition also includes an isocyanate-functional compound as a crosslinker. The coating composition forms a corrosion-resistant film when applied directly to the substrate surface without a pretreatment or primer.
1 . A urethane coating composition, comprising:
(1) a polyol that is the reaction product of
a) a resin having the general formula (I)
wherein:
each A is independently a substituted or unsubstituted divalent aliphatic group having from 1 to about 6 carbon atoms, an unsubstituted divalent aromatic group having from 6 to about 10 carbon atoms, a divalent aromatic group substituted with an organic group having from 1 to 4 carbon atoms (C1-C4 alkyl or alkenyl), a halogen, —OR′O, wherein R′ is unsubstituted or substituted C 1 -C 4 alkyl, —C(O)—, —O—, —S—, —S(O)—, or —(SO) 2 ;
each Ph is independently a an unsubstituted phenylene ring, or a phenylene ring substituted with H, C1-C4 alkyl, Cl, Br, or —OR;
each R is independently H, C1-C4 alkyl, or an epoxide of the formula
wherein R 1 is independently H, unsubstituted C 1 -C 4 alkyl, or C 1 -C 4 alkyl substituted with —OH, or C 1 -C 4 alkoxy;
m is 0 or 1; and
n is between 0 and 6; and
(b) an acid or diol present in an amount sufficient to react substantially all the epoxide groups, if present, in component (a), wherein the reaction is carried out in the presence of a reaction catalyst; and
an isocyanate-functional compound.
2 . The coating composition of claim 1 , wherein each R in the general formula (I) is an epoxide wherein each R 1 and R 2 is independently —CH 2 — or H.
3 . The coating composition of claim 1 , wherein each A in the general formula (I) is a methylene group and m is 1.
4 . The coating composition of claim 1 , wherein each A in the general formula (I) is a phenylene ring substituted with an —OR′O— group, wherein R′ is —CH 2 —CH(OH)—CH 2 —, and m is 0.
5 . The coating composition of claim 1 , wherein each Ph is independently an unsubstituted phenylene ring or a phenylene ring substituted with an —OR group, wherein R is an epoxide of the formula
wherein each R 1 is independently —CH 2 — or H.
6 . The coating composition of claim 1 , wherein each Ph is independently an unsubstituted phenylene ring or a phenylene ring substituted with a dimethylbenzyl group.
7 . The coating composition of claim 1 , wherein n is between 1.0 and 2.0.
8 . The coating composition of claim 1 , wherein the resin of general formula (I) has the structure:
wherein n is between 1.0 and 2.0.
9 . The coating composition of claim 1 , wherein the acid is an aromatic acid selected from an unsubstituted aromatic acid, alkyl substituted aromatic acid, alkenyl substituted aromatic acid, or hydroxy substituted aromatic acid.
10 . The coating composition of claim 8 , wherein the aromatic acid is benzoic acid.
11 . The coating composition of claim 1 , wherein the amount of acid or diol sufficient to react substantially all the epoxide groups is about 1 to 5 moles.
12 . The coating composition of claim 1 , wherein the amount of acid or diol sufficient to react substantially all the epoxide groups is about 2 to 4 moles.
13 . The coating composition of claim 1 , wherein the reaction catalyst is selected from trialkyl amines, dialkylaryl amines, salts of quarternary ammonium compounds, salts of quarternary phosphonium compounds, and alkali metal halides.
14 . The coating composition of claim 1 , wherein the polyol has an OH number of about 150 to 350.
15 . The coating composition of claim 1 , wherein the OH:NCO ratio of the urethane composition is about 0.5:1 to 2:1.
16 . The coating composition of claim 1 , wherein the resin of general formula (I) has the structure:
and n is 0.05 to 0.1.
17 . The coating composition of claim 1 , wherein the diol is an aliphatic diol selected from unsubstituted or alkyl-substituted propanediol, butanediol, pentanediol, hexanediol, and mixtures thereof.
18 . The coating composition of claim 1 , wherein the diol is 1,4-butanediol.
19 . The coating composition of claim 1 , wherein the reaction catalyst is dimethylbenzylamine.
20 . The coating composition of claim 1 , wherein the isocyanate-functional compound is a polyisocyanate selected from selected from 2,4-toluenediisocyanate, 2,6-toluenediisocyanate, 4,4′ -methylenediphenyldiisocyanate, hexamethylenediisocyanate, polymethylene-polyphenylisocyanate, cyclic trimers, cocyclic trimers, and mixtures thereof.