Coating compositions for roofing granules, dark colored roofing granules with increased solar heat reflectance, solar heat-reflective shingles and process for producing the same
Dark colored roofing granules include an inert base particle coated with a composition including a metal silicate, a non-clay latent heat reactant, and a dark colored but solar reflective pigment.
1. A plurality of dark-colored roofing granules, each of the dark-colored roofing granules comprising:
an inert base particle; and
a cured coating disposed about the inert base particle, the cured coating being a reaction product of a coating composition comprising:
an alkali metal silicate;
at least one non-clay latent heat reactant; and
at least one inorganic solar heat-reflective pigment, each of the at least one inorganic solar heat-reflective pigments having an L* less than 30 and a solar reflectance greater than 20 percent, and wherein the coating composition comprises at least about 5 percent to 25 percent of the at least one solar heat-reflective pigment,
wherein
the plurality of dark-colored roofing granules has an L* less than 30 and a solar reflectance greater than 20, and
wherein each of the dark-colored roofing granules lacks a light-colored base coat disposed between the inert base particle and the cured coating.
2. A plurality of dark-colored roofing granules according to claim 1 , wherein in the coating composition the at least one non-clay latent heat reactant is selected from the group consisting of Portland cement, aluminum fluoride, ammonium silicofluoride, alkali metal silicofluorides, and alkaline earth metal silicofluorides.
3. A plurality of dark-colored roofing granules according to claim 1 , wherein in the coating composition the at least one non-clay latent heat reactant comprises Portland cement, aluminum fluoride and at least one alkali metal silicofluoride.
4. A plurality of dark-colored roofing granules according to claim 3 , wherein in the coating composition the at least one alkali metal silicofluoride is sodium silicofluoride.
5. A plurality of dark-colored roofing granules according to claim 3 , wherein in the coating composition wherein the at least one non-clay latent heat reactant comprise from about 3 to 15 weight percent of the coating composition of aluminum fluoride, from about 0.5 to 5 weight percent of the coating composition of sodium silicofluoride, and from about 0.5 to 5 weight percent of the coating composition of Portland cement.
6. A plurality of dark-colored roofing granules according to claim 1 , wherein in the coating composition wherein the at least one inorganic solar heat-reflective pigment is selected from the group consisting of Arctic Black 10C909 (chromium green-black), Black 411 (chromium iron oxide), Brown 12 (zinc iron chromite), Brown 8 (iron titanium brown spinel), and Yellow 193 (chrome antimony titanium), 56, Eclipse Black 10201, Forest Green 10241, Eclipse Black 10202, Eclipse Black 10203, and H IR Green V-12650.
7. A plurality of dark-colored roofing granules of claim 1 wherein in each of the dark-colored roofing granules the cured coating comprises a first layer including a first metal silicate binder and a first inorganic solar heat-reflective pigment and a second layer including a second metal silicate binder and a second inorganic solar heat-reflective pigment.
8. A plurality of dark-colored roofing granules of claim 7 wherein in each of the dark-colored roofing granules the second inorganic solar heat-reflective pigment is identical to the first inorganic solar heat-reflective pigment.
9. A plurality of dark-colored roofing granules of claim 8 wherein in each of the dark-colored roofing granules the first and second inorganic solar heat-reflective pigments are selected from the group consisting of Arctic Black 10C909 (chromium green-black), Black 411 (chromium iron oxide), Brown 12 (zinc iron chromite), Brown 8 (iron titanium brown spinel), and Yellow 193 (chrome antimony titanium), Brown 10364, Eclipse Black 10201, Forest Green 10241, Eclipse Black 10202, Eclipse Black 10203, and H IR Green V-12650.
10. A plurality of dark-colored roofing granules of claim 8 wherein in each of the dark-colored roofing granules the first coating layer comprises at least about 30 percent to about 40 percent of the first inorganic solar heat-reflective pigment, and wherein the second coating layer comprises at least about 30 percent to about 40 percent of the second inorganic solar heat-reflective pigment.
11. A plurality of dark-colored roofing granules of claim 7 wherein in each of the dark-colored roofing granules the first and second coating layers form from about 4 percent by weight of the inert base particle to about 10 percent by weight of the inert base particle.
12. A plurality of dark-colored roofing granules of claim 7 wherein each of the dark-colored roofing granules further comprises a third coating layer, the third coating layer being identical to the second coating layer and the first coating layer.
13. A plurality of dark-colored roofing granules of claim 7 wherein in each of the dark-colored roofing granules the second inorganic solar heat-reflective pigment is different from the first inorganic solar heat-reflective pigment.
14. A plurality of dark-colored roofing granules of claim 13 wherein in each of the dark-colored roofing granules the first inorganic solar heat-reflective pigment is selected from the group consisting of Arctic Black 10C909 (chromium green-black), Black 411 (chromium iron oxide), Brown 12 (zinc iron chromite), Brown 8 (iron titanium brown spinel), and Yellow 193 (chrome antimony titanium), Brown 10364, Eclipse Black 10201, Forest Green 10241, Eclipse Black 10202, Eclipse Black 10203, and H IR Green V-12650.
15. A plurality of dark-colored roofing granules of claim 13 wherein in each of the dark-colored roofing granules the second inorganic solar heat -reflective pigment is selected from the group consisting of Arctic Black 10C909 (chromium green-black), Black 411 (chromium iron oxide), Brown 12 (zinc iron chromite), Brown 8 (iron titanium brown spinel), and Yellow 193 (chrome antimony titanium), Brown 10364, Eclipse Black 10201, Forest Green 10241, Eclipse Black 10202, Eclipse Black 10203, and H IR Green V-12650.
16. A plurality of dark-colored roofing granules of claim 13 wherein in each of the dark-colored roofing granules the second layer further comprises an inorganic solar-reflective functional pigment.
17. A plurality of dark-colored roofing granules of claim 16 wherein in each of the dark-colored roofing granules the solar-reflective functional pigment is selected from the group consisting of mirrorized silica flakes, metal flake pigments, and metal oxide coated flake pigments.
18. A plurality of dark-colored roofing granules of claim 16 wherein in each of the dark-colored roofing granules the second coating layer comprises at least about 1 percent to about 60 percent of the solar-reflective functional pigment.
19. A plurality of dark-colored roofing granules of claim 16 wherein in each of the dark-colored roofing granules the second coating layer comprises at least about 1 percent to about 60 percent of the second solar heat-reflective pigment.
20. A plurality of dark-colored roofing granules of claim 1 , wherein in each of the dark-colored roofing granules the inert base particle is an inert mineral particle and the cured coating is disposed directly on the inert mineral particle.
21. A plurality of dark-colored roofing granules of claim 1 , wherein in each of the dark-colored roofing granules the coating composition further includes aluminum oxide having a particle size in the range of 0.1 to 5 micrometers.
22. A plurality of dark-colored roofing granules of claim 1 , wherein in each of the dark-colored roofing granules the coating composition is free of kaolin clay.
23. A plurality of dark-colored roofing granules of claim 1 , wherein in each of the dark-colored roofing granules the at least one inorganic solar heat-reflective pigment is a metal oxide pigment.
24. A plurality of dark-colored roofing granules of claim 1 , wherein in each of the dark-colored roofing granules the at least one inorganic pigment is the only pigment in the coating composition.
25. A plurality of dark-colored roofing granules of claim 1 , wherein in each of the dark-colored roofing granules the inorganic solar heat-reflective pigments does not comprise a white pigment coated with a near infrared-absorbing colorant.
26. An asphalt shingle having a surface coated with the plurality of dark-colored roofing granules of claim 1 , the shingle having an L* less than 55 and a solar reflectance of greater than 20 percent.
27. An asphalt shingle having a surface coated with the plurality of dark-colored roofing granules of claim 1 , the shingle having an L* less than 30 and a solar reflectance of greater than 20 percent.