Methods of continuously casting new 6xxx aluminum alloys, and products made from the same
New 6xxx aluminum alloy strips having an improved combination of properties are disclosed. The new 6xxx new aluminum alloy strips are rolled to a target thickness in-line via at least a first rolling stand and a second rolling stand. In one approach, the 6xxx new aluminum alloy strips may contain 0.8 to 1.25 wt. % Si, 0.2 to 0.6 wt. % Mg, 0.5 to 1.15 wt. % Cu, 0.01 to 0.2 wt. % manganese, 0.01 to 0.2 wt. % iron; up to 0.30 wt. % Ti; up to 0.25 wt. % Zn; up to 0.15 wt. % Cr; and up to 0.18 wt. % Zr.
1. A 6xxx aluminum alloy strip (“6AAS”) having a thickness of from 0.1524 to 4.064 mm;
wherein the 6AAS consists essentially of 0.8 to 1.25 wt. % Si, 0.2 to 0.6 wt. % Mg, 0.5 to 1.15 wt. % Cu, 0.01 to 0.20 wt. % Mn, 0.01 to 0.3 wt. % Fe; up to 0.30 wt. % Ti; up to 0.25 wt. % Zn; up to 0.15 wt. % Cr; and up to 0.18 wt. % Zr, the balance being aluminum and impurities;
wherein the 6AAS realizes an average second phase particle cluster number density of at least 4300 clusters per mm 2 .
2. The 6xxx aluminum alloy strip of claim 1 , wherein the 6xxx aluminum alloy strip realizes a Delta R of not greater than 0.10.
3. The 6xxx aluminum alloy strip of claim 1 , wherein the 6xxx aluminum alloy strip in the T6 temper realizes a longitudinal tensile yield strength of from 160 to 350 MPa.
4. The 6xxx aluminum alloy strip of claim 1 , wherein the 6xxx aluminum alloy strip in the T4 temper realizes a longitudinal tensile yield strength of from 100 to 200 MPa.
5. The 6xxx aluminum alloy strip of claim 1 , wherein the 6xxx aluminum alloy strip realizes a FLD o of 28.0 to 35.0 (Engr %), wherein the FLD o is measured at a gauge of 1.0 mm.
6. The 6xxx aluminum alloy strip of claim 1 , wherein the 6AAS realizes an average second phase particle cluster number density of at least 4500 clusters per mm 2 .
7. The 6xxx aluminum alloy strip of claim 1 , wherein the 6AAS realizes an average second phase particle cluster number density of at least 5000 clusters per mm 2 .
8. The 6xxx aluminum alloy strip of claim 1 , wherein the 6AAS realizes an average second phase particle cluster number density of at least 5500 clusters per mm 2 .
9. The 6xxx aluminum alloy strip of claim 1 , wherein the 6AAS realizes an average second phase particle cluster number density of at least 6000 clusters per mm 2 .
10. The 6xxx aluminum alloy strip of claim 9 , wherein the 6AAS realizes all of:
(i) a Delta R of not greater than 0.10; and
(ii) an FLD o of at least 30.0 (Engr %) in a T4 temper, wherein the FLD o is measured at a gauge of 1.0 mm; and
(iii) a TYS of at least 180 MPa in a T6 temper.
11. The 6xxx aluminum alloy strip of claim 10 , wherein the 6AAS realizes a depth of attack of not greater than 300 microns when tested in accordance with ISO 11846 (1995).