Production method for plated steel sheet using a steel sheet annealing device
Provided is a method for producing plated steel sheet by means of an annealing device which includes at least one section and in which the at least one section is filled with a gas constituting a non-reducing atmosphere or a weakly reducing atmosphere to substantially improve the quality of plating onto hot-dipped steel sheet, including the plating properties, alloying properties, anti-pickup properties, plating adhesion properties, anti-flaking properties, anti-cratering properties and anti-ash properties, by using prior-art annealing equipment and heat-treatment cycle without any additional oxidation-reduction heat treatment process or large quantities of high-cost alloying elements.
1. A plated steel sheet manufacturing method including:
an annealing process for annealing a steel sheet by supplying a non-reducing atmospheric gas from the start of the annealing process to the end of the annealing process, and
a plating process for plating the annealed steel sheet,
wherein the non-reducing atmospheric gas contains nitrogen (N 2 ) of 100 vol % and has a dew-point temperature of −30° C. to −10° C.
2. The method of claim 1 , wherein the annealing process includes at least one operation selected from the group consisting of pre heating, heating, soaking, slow cooling, rapid cooling, and final cooling.
3. The method of claim 2 , wherein the annealing process further includes at least one of overaging and re-heating operations.
4. The method of claim 1 , wherein the plated steel sheet is one of a hot-dip galvanized steel sheet, a galvannealed steel sheet, a galvanium plated steel sheet, an aluminum plated steel sheet and a zinc-magnesium-based plated steel sheet.