Steam turbine rotor, steam turbine including same, and thermal power plant using same
View Patent ↗It is an objective of the invention to provide a steam turbine rotor of which a rotor shaft is made of a low-cost heat resistant ferritic steel and that can withstand high main steam temperatures of about 650° C. There is provided a steam turbine rotor comprising: a rotor shaft made of a heat resistant ferritic steel such as a 12-Cr steel; and a rotor blade made of a Ti—Al alloy, wherein the Ti—Al alloy includes: from 38 to 45 atomic % of Al; from 0.5 to 2 atomic % of V; from 2 to 6 atomic % of Cr and/or Mo; and the balance being Ti and incidental impurities.
1. A steam turbine rotor to be used for steam having a temperature of about 650 to 670° C. comprising:
a rotor shaft made of a heat resistant ferritic steel of a 12-Cr steel; and
a blade made of a titanium-aluminum alloy,
wherein the titanium-aluminum alloy includes: from 38 to 44.5 atomic % of aluminum; from 0.5 to 2 atomic % of vanadium; one of or both of chromium and molybdenum in a total amount from 2 to 6 atomic %; and the balance being titanium and incidental impurities,
wherein the titanium-aluminum alloy may optionally further include: one or more of niobium, tantalum, tungsten, iron, manganese and nickel in a total amount from 0.5 to 3 atomic %; and/or from 0.05 to 0.2 atomic % of boron, and
wherein the 12-Cr steel consists of: from 0.05 to 0.30 mass % of carbon; 0.2 or less mass % of silicon; from 0.01 to 1.5 mass % of manganese; from 0.005 to 0.3 mass % of nickel; from 8.5 to 11.0 mass % of chromium; from 0.05 to 0.5 mass % of molybdenum; from 1.0 to 3.0 mass % of tungsten; from 0.05 to 0.30 mass % of vanadium; from 0.01 to 0.20 mass % of niobium; from 0.5 to 2.5 mass % of cobalt; from 0.01 to 1.0 mass % of rhenium; from 0.01 to 0.1 mass % of nitrogen; from 0.001 to 0.030 mass % of boron; from 0.0005 to 0.006 mass % of aluminum; and the balance being iron and incidental impurities.
2. The steam turbine rotor according to claim 1 , wherein the titanium-aluminum alloy of the blade has a forged microstructure.
3. A steam turbine, comprising a high pressure stage including the steam turbine rotor according to claim 1 .
4. A steam turbine, comprising a high pressure stage including the steam turbine rotor according to claim 2 .
5. A thermal power plant, comprising the steam turbine according to claim 3 .
6. The steam turbine rotor according to claim 1 , wherein a passivation film for steam oxidation resistance is coated on a surface of the blade.