Highly selective catalyst and method of isomerization of C4—C7 paraffin hydrocarbons
View Patent ↗The invention relates to isomerization catalysts and can be used in the petroleum processing and petrochemical industry. The catalyst contains sulfated zirconium oxide and a binder—aluminum oxide in a ratio of ZrO2/SO4 to Al2O3 from 70 to 30 to 90 to 10, as well as promoter, a group II metal, Ca, in a quantity ranging from 0.01 to 1 wt % of the weight of the catalyst. The catalyst also contains platinum and/or palladium in a quantity ranging from 0.1 to 0.45 wt % of the metal. Isomerization of C4-C7 paraffinic hydrocarbons in the presence of hydrogen at a temperature of 110-200° C., a pressure of 1-5 MPa, a hydrogen:hydrocarbon ratio of 0.5-4, and a feedstock space velocity of 0.5-4 h −1 is carried out on a catalyst having the claimed composition. The proposed catalyst offers an enhanced degree of isomerization, improved selectivity of the process, and increased strength of the granules.
1. An isomerization catalyst for C4-C7 paraffinic hydrocarbons, the catalyst comprising a sulfated zirconium oxide, an inorganic oxide as a binder, a group VIII metal as a hydrogenating component, and a group II metal as a promoter, the catalyst being made at least by mixing powders of a sulfated zirconium hydroxide and an inorganic oxide and/or hydroxide binder, a solution of a group II metal inorganic salt, and a nitric acid and sulfuric acid solution, wherein the content of the group II metal promoter in the isomerization catalyst is greater than 0.5 wt. % and less than 1 wt. %.
2. The catalyst according to claim 1 , wherein the group II metal used as the promoter is calcium added in a form of calcium chloride and/or nitrate.
3. The catalyst according to claim 1 , wherein an aluminum oxide and/or hydroxide is used as a binder, wherein a ratio of the sulfated zirconium oxide to the aluminum oxide in the isomerization catalyst ranges from 7:3 up to 9:1.
4. The catalyst according to claim 1 , wherein platinum and/or palladium in an amount of 0.1-0.45 wt % are used as the group VIII metal.
5. The catalyst according to claim 1 , wherein the content of sulfate ions in the zirconium oxide is no less than 5% of a calcined material.
6. The catalyst according to claim 1 , wherein the catalyst provides a selectivity to an isomerizate greater than that of a catalyst comprising no group II metal promoter.
7. The catalyst according to claim 1 , wherein the catalyst exhibits a strength of catalyst granules greater than that of a catalyst comprising no group II metal promoter.