Disclosed is a lithium secondary battery, including a cathode, an anode and a non-aqueous electrolyte, wherein the cathode includes a cathode active material containing lithium-metal oxide of which at least one of metals has a concentration gradient region between a core part and a surface part thereof, and the anode includes hard carbon having an average lattice distance (d 002 ) in the range of 3.6 to 3.8 Å and graphite having-an average lattice distance (d 002 ) in the range of 3.356 to 3.360 Å, such that output and high-temperature storage properties may be improved.
1. A lithium secondary battery, comprising a cathode, an anode and a non-aqueous electrolyte,
wherein the cathode includes a cathode active material containing lithium-metal oxide, the lithium metal oxide containing Ni, Co, and Mn, wherein at least one of Ni, Co, and Mn has a decreasing or increasing concentration gradient between a core part and a surface part thereof in a direction from the core part to the surface part, and
the anode includes hard carbon having an average lattice distance (d 002 ) in the range of 3.6 to 3.8 Å and graphite having an average lattice distance (d 002 ) in the range of 3.356 to 3.360 Å.
2. The lithium secondary battery according to claim 1 , wherein the concentration of Mn is increased between the core part and the surface part in the direction from the core part to the surface part, and the concentration of Ni is decreased between the core part and the surface part in the direction from the core part to the surface part.
3. The lithium secondary battery according to claim 1 , wherein Co has a constant concentration throughout the cathode active material from the core part to the surface part.
4. The lithium secondary battery according to claim 1 , wherein the lithium-metal oxide is represented by Formula 1 below,
Li x M1 a M2 b M3 c O y , [Formula 1]
wherein M1, M2 and M3 are Ni, Co, and Mn, respectively, and
0<x≤1.1, 2≤y≤2.02, 0<a≤1, 0<b≤1, 0<c≤1, and 0<a+b+c≤1.
5. The lithium secondary battery according to claim 4 , wherein 0.6≤a≤0.95 and 0.05≤b+c≤0.4.
6. The lithium secondary battery according to claim 4 , wherein 0.7≤a≤0.9 and 0.1≤b+c≤0.3.
7. The lithium secondary battery according to claim 1 , wherein the lithium-metal oxide has a primary particle of a rod-type shape.
8. The lithium secondary battery according to claim 1 , wherein a mixing weight ratio of the hard carbon and the graphite is 1:99 to 99:1.
9. The lithium secondary battery according to claim 1 , wherein a mixing weight ratio of the hard carbon and the graphite is 5:95 to 70:30.