Formation of hydrated nanocellulose sheets with or without a binder for the use as a dermatological treatment
The present invention is a hydrated, nanocellulose nonwoven sheet and method for manufacturing the nanocellulose sheet having dermatologically active ingredients. The sheet is formed through a high pressure or vacuum filtration process from a dilute suspension. This suspension, which contains the nanocellulose, may also contain dermatologically active ingredients. The dermatologically active ingredients are incorporated into the unwoven sheet. The dilute suspension may contain binding agents that improve the strength of the nonwoven nanocellulose sheet. These binding agents can also be cross-linked after the formation of the sheet by applying other chemical agents or treating the sheet after formation.
1. A method of manufacture for forming a hydrated, nonwoven nanocellulose sheet, said method comprising the steps of:
providing an amount of nanocellulose;
forming a first suspension by diluting said amount of nanocellulose into a suspension medium;
forming a binding agent solution by adding a binding agent to said first suspension to a mass concentration of 0.01 grams per liter to 10 grams per liter;
forming a cross-linking solution by diluting a cross-linking agent in a solvent to a mass concentration of 0.001 grams per liter to 20 grams per liter to form a cross-linking solution;
forming a gel by dispensing said binding agent solution into said cross-linking solution;
collecting said gel from said cross-linking solution;
forming a second suspension by re-dispersing said gel into a solvent; and
forming the hydrated, nonwoven nanocellulose sheet by placing said second suspension into a dispensing device to filter said second suspension.
2. The method of manufacture of claim 1 , further comprising the step of cutting said sheet into a predetermined shape and size.
3. The method of manufacture of claim 2 , further comprising the step of packaging said sheet after the cutting step.
4. The method of manufacture of claim 1 , further comprising the step of
adding an amount of a dermatologically active ingredient to said first suspension after forming said first suspension.
5. The method of manufacture of claim 4 , wherein said dermatologically active ingredient comprises an oil component and an alkyl-modified carboxyvinyl polymer component.
6. The method of manufacture of claim 4 , wherein a diameter of said nanocellulose is 5 to 100 nm and a length of said nanocellulose is up to 10 microns.
7. The method of manufacture of claim 4 , wherein said dermatologically active ingredient is selected from the group consisting of silver, collagen proteins, fragrances, and antioxidants.
8. The method of manufacture of claim 7 , further comprising the step of cutting said sheet into a predetermined shape and size.
9. The method of manufacture of claim 8 , further comprising the step of packaging said sheet after the cutting step.
10. The method of manufacture of claim 8 , wherein said predetermined shape and size is a facial mask.
11. The method of manufacture of claim 7 , wherein said dermatologically active ingredient comprises an oil component and an alkyl-modified carboxyvinyl polymer component.