Pet chew toys of rubber and polyamide, and methods of manufacture thereof
View Patent ↗A pet chew toy comprising a blend containing a polyamide terpolymer and a diene elastomer, wherein the diene elastomer is crosslinked and the polyamide terpolymer has a Tm in the range of 120° C. to 250° C.
1. A pet chew toy, comprising:
two end portions formed from a first material composition, the first material composition having a first Shore durometer hardness; and
a central shaft portion joined to the two end portions, the central shaft portion formed from a second material composition having a second Shore durometer hardness that is less than the first Shore durometer hardness;
wherein:
the first material composition comprises a blend containing a polyamide terpolymer and a crosslinked diene elastomer;
said polyamide terpolymer is formed of three different polyamide segments and has a Tm in the range of 120° C. to 250° C.;
the second material comprises an elastomer.
2. The pet chew toy of claim 1 wherein said Tm is in the range of 120° C. to 200° C.
3. The pet chew toy of claim 1 wherein said Tm is in the range of 120° C. to 150° C.
4. The pet chew toy of claim 1 wherein said three different polyamide segments are the following three polyamide homopolymer segments:
5. The pet chew toy of claim 1 wherein said polyamide terpolymer comprises 30% by weight to 95% by weight of the first material composition.
6. The pet chew toy of claim 1 wherein said crosslinked diene elastomer comprises 5% by weight to 50% by weight of the first material composition.
7. The pet chew toy of claim 1 wherein the polyamide terpolymer and the crosslinked diene elastomer of the first material composition are each present at a selected weight percent, and the weight ratio of the crosslinked diene elastomer to the polyamide terpolymer ranges from 1:10 to 1:1.
8. The pet chew toy of claim 1 wherein said crosslinked diene elastomer of the first material composition comprises crosslinked cis-1,4-polyisoprene.
9. A pet chew toy, comprising:
two end portions formed from a first material composition; and
a central shaft portion joined to the two end portions, the central shaft formed from a second material composition;
wherein:
the first and second material compositions comprise first and second blends, respectively, containing a polyamide terpolymer formed of three different polyamide segments and a crosslinked diene elastomer, wherein the total amount of the polyamide terpolymer in the first and second material compositions ranges from 30 to 95% by weight of the pet chew;
the melting point (Tm) of the polyamide terpolymer is in the range of 120° C. to 200° C.;
the crosslinked diene elastomer comprises crosslinked cis-1,4-polyisoprene; and
said polyamide terpolymer is a terpolymer of the following three polyamide homopolymer segments:
10. The pet chew toy of claim 9 wherein said Tm ranges from 120° C. to 150° C.
11. A pet chew toy comprising:
two end portions formed from a first material composition; and
a central shaft portion between the two end portions and formed from a second material composition;
wherein:
the first material composition comprises a first blend of a polyamide terpolymer formed of three different polyamide segments and a crosslinked diene elastomer;
the second material composition comprises a second blend of said polyamide terpolymer formed of three different polyamide segments and said crosslinked diene elastomer;
said polyamide terpolymer has a melting temperature, Tm, in the range of 120° C. to 250° C.; and
the amount of crosslinked diene elastomer in the first blend differs from the amount of crosslinked diene elastomer in the second blend.
12. The pet chew toy of claim 11 wherein said polyamide terpolymer has a Tm in the range of 120° C. to 200° C.
13. The pet chew toy of claim 11 wherein said polyamide terpolymer has a Tm in the range of 120° C. to 150° C.
14. The pet chew toy of claim 11 wherein said crosslinked diene elastomer comprises crosslinked cis-1,4-polyisoprene.
15. A pet chew toy comprising:
two end portions formed from a first material composition; and
a central shaft portion between the two end portions and formed from a second material composition;
wherein:
the first material composition comprises a first blend of a polyamide terpolymer formed of three different polyamide segments and a crosslinked diene elastomer;
the second material composition comprises a second blend of said polyamide terpolymer formed of three different polyamide segments and said crosslinked diene elastomer;
said polyamide terpolymer has a melting temperature Tm in the range of 120° C. to 250° C.;
the amount of crosslinked diene elastomer in the first blend differs from the amount of crosslinked diene elastomer in the second blend; and
polyamide terpolymer is a terpolymer of the following three polyamide homopolymer segments: