Highly formable automotive aluminum sheet with reduced or no surface roping and a method of preparation
View Patent ↗Disclosed are novel processes to increase productivity on a continuous anneal and solution heat treatment line for heat-treatable automotive aluminum sheet products with high T4 and after-paint bake strengths and reduced roping. As a non-limiting example, the processes described herein can be used in the automotive industry. The disclosed heat treatable alloys and processes also may be applicable to the marine, aerospace, and transportation industries.
1. An aluminum alloy comprising about 0.20-1.0 wt. % Si, 0.11-0.40 wt. % Fe, 0.0-0.23 wt. % Cu, 0.0-0.22 wt. % Mn, 0.50-0.83 wt. % Mg, 0.0-0.25 wt. % Cr, 0.0-0.006 wt. % Ni, 0.0-0.15 wt. % Zn, 0.0-0.17 wt. % Ti, up to 0.15 wt. % impurities, with the remainder as Al, wherein the aluminum alloy comprises a yield strength of at least 100 MPa when the aluminum alloy is in a T4 temper.
2. The aluminum alloy of claim 1 , comprising about 0.60-0.95 wt. % Si, 0.20-0.35 wt. % Fe, 0.05-0.20 wt. % Cu, 0.05-0.20 wt. % Mn, 0.55-0.75 wt. % Mg, 0.0-0.15 wt. % Cr, 0.0-0.006 wt. % Ni, 0.0-0.15 wt. % Zn, 0.0-0.15 wt. % Ti, up to 0.15 wt. % impurities, with the remainder as Al.
3. A motor vehicle body part comprising an aluminum alloy comprising about 0.20-1.0 wt. % Si, 0.11-0.40 wt. % Fe, 0.0-0.23 wt. % Cu, 0.0-0.22 wt. % Mn, 0.50-0.83 wt. % Mg, 0.0-0.25 wt. % Cr, 0.0-0.006 wt. % Ni, 0.0-0.15 wt. % Zn, 0.0-0.17 wt. % Ti, up to 0.15 wt. % impurities, with the remainder as Al, wherein the aluminum alloy comprises a yield strength of at least 100 MPa when the aluminum alloy is in a T4 temper.
4. The motor vehicle body part of claim 3 , wherein the motor vehicle body part comprises an outer panel.
5. An aluminum alloy comprising about 0.20-1.0 wt. % Si, 0.11-0.40 wt. % Fe, 0.0 0.23 wt. % Cu, 0.0-0.22 wt. % Mn, 0.50-0.83 wt. % Mg, 0.0-0.25 wt. % Cr, 0.0-0.006 wt. % Ni, 0.0-0.15 wt. % Zn, 0.0-0.17 wt. % Ti, up to 0.15 wt. % impurities, with the remainder as Al, wherein the aluminum alloy comprises a yield strength of at least 100 MPa when the aluminum alloy is in a T6 temper.
6. The aluminum alloy of claim 5 , comprising about 0.60-0.95 wt. % Si, 0.20-0.35 wt. % Fe, 0.05-0.20 wt. % Cu, 0.05-0.20 wt. % Mn, 0.55-0.75 wt. % Mg, 0.0-0.15 wt. % Cr, 0.0-0.006 wt. % Ni, 0.0-0.15 wt. % Zn, 0.0-0.15 wt. % Ti, up to 0.15 wt. % impurities, with the remainder as Al.
7. A motor vehicle body part comprising an aluminum alloy comprising about 0.20-1.0 wt. % Si, 0.11-0.40 wt. % Fe, 0.0-0.23 wt. % Cu, 0.0-0.22 wt. % Mn, 0.50-0.83 wt. % Mg, 0.0-0.25 wt. % Cr, 0.0-0.006 wt. % Ni, 0.0-0.15 wt. % Zn, 0.0-0.17 wt. % Ti, up to 0.15 wt. % impurities, with the remainder as Al, wherein the aluminum alloy comprises a yield strength of at least 100 MPa when the aluminum alloy is in a T6 temper.
8. The motor vehicle body part of claim 7 , wherein the motor vehicle body part comprises an outer panel.