Light weight proppant with improved strength and methods of making same
Methods are described to make strong, tough, and/or lightweight glass-ceramic composites having a crystalline phase and an amorphous phase generated by viscous reaction sintering of a complex mixture of oxides and other materials. The present invention further relates to strong, tough, and lightweight glass-ceramic composites that can be used as proppants and for other uses.
1. A method to prop open subterranean formation fractures comprising: introducing a proppant formulation comprising a proppant into a subterranean formation, wherein the proppant comprises a sintered body, wherein said sintered body comprises at least one crystalline phase, at least one amorphous phase, at least one mullite whisker phase, and substantially spherical microspheres and/or pores uniformly distributed in said sintered body, said spherical microspheres and/or pores comprising gas bubbles.
2. A method of treating a subterranean producing zone penetrated by a well bore comprising the steps of:
a. preparing or providing a treating fluid that comprises a fluid, energized fluid, foam, or a gas carrier having a proppant suspended therein, wherein the proppant comprises a sintered body, wherein said sintered body comprises at least one crystalline phase, at least one amorphous phase, at least one mullite whisker phase, and substantially spherical microspheres and/or pores uniformly distributed in said sintered body, said spherical microspheres and/or pores comprising gas bubbles, and
b. pumping said treating fluid into said subterranean producing zone whereby said proppant is deposited therein.
3. The method of claim 2 , wherein said treating fluid is a fracturing fluid and said proppant is deposited in fractures formed in said subterranean producing zone.
4. The method of claim 2 , wherein said treating fluid is a gravel packing fluid and said proppant is deposited in said well bore adjacent to said subterranean producing zone.
5. The method of claim 2 , wherein said crystalline phase is continuous and uniformly distributed throughout said sintered body.
6. The method of claim 2 , wherein said crystalline phase is discontinuous and uniformly distributed throughout said sintered body.
7. The method of claim 2 , wherein said pores have a smooth, glassy interior surface.
8. The method of claim 2 , further comprising a template, wherein said sintered body encapsulates said template.
9. The method of claim 8 , wherein said template is a sphere.
10. The method of claim 8 , wherein said template is a hollow sphere.
11. The method of claim 8 , wherein said template is a cenosphere.
12. The method of claim 8 , wherein said template comprises whiskers and at least one amorphous phase.
13. The method of claim 2 , wherein said proppant has at least one of the following characteristics:
a. an overall diameter of from about 90 microns to about 2,000 microns;
b. a Krumbein sphericity of at least about 0.5 and a roundness of at least about 0.5;
c. a crush strength of about 1400 psi or greater;
d. a specific gravity of from about 1.0 to about 3.0;
e. a porosity of from about 1% to about 70% by weight;
f. at least 90% (by distribution) of the microspheres and/or pores having a pore size of from about 0.1 μm to about 10 μm, and
g. microspheres and/or pores have a smooth, glassy interior surface, and
at least 80% (by distribution) of proppant pores are not in contact with each other.
14. The method of claim 2 , comprising a sintered sphere having a Krumbein sphericity of at least about 0.5 and a roundness of at least about 0.4, and wherein said sphere comprises a) at least one crystalline phase and b) at least one amorphous phase, c) a plurality of microspheres and, optionally, d) ceramic whiskers, wherein said sintered sphere has a diameter of from about 90 microns to 2,500 microns, and said sintered sphere has a specific gravity of from 0.8 g/cc to about 3.8 g/cc, and said proppant has a crush strength of from about 1,000 psi or greater, and wherein said proppant includes one or more of the following characteristics:
1) said crystalline phase is present in an amount of at least 30% by weight, based on the weight of the proppant;
2) said amorphous phase is present in an amount of at least 10% by weight, based on the weight of the proppant;
3) said proppant having a porosity from about 1% to 70% by weight where
porosity
(
%
)
=
100
-
(
S
G
m
S
G
t
)
×
100
and
SG m =measured specific gravity and
SG t =theoretical specific gravity;
4) said proppant having a porosity from about 5% to 50% by weight;
5) said proppant having a porosity from about 3% to 20% by weight;
6) said proppant having a porosity from about 4% to 16% by weight;
7) said proppant having a specific gravity of from 1.6 to 1.8 with a crush strength of at least 2000 psi;
8) said proppant having a specific gravity of from 1.8 to 2 with a crush strength of at least 3000 psi;
9) said proppant having a specific gravity of from 2 to 2.1 with a crush strength of at least 5,000 psi;
10) said proppant having a specific gravity of from 2.25 to 2.35 with a crush strength of at least 8,000 psi;
11) said proppant having a specific gravity of from 2.5 to 3.2 with a crush strength of at least 18,000 psi;
12) said proppant having a specific gravity of from 2.5 to 3.2 with a crush strength of at least 30,000 psi;
13) said proppant having a combined clay amount and cristobalite amount of less than 20% by weight of proppant;
14) said proppant having a free alpha-alumina content of at least 5% by weight of said proppant;
15) said proppant having an HF etching weight loss of less than 35% by weight of said proppant;
16) said proppant having said microspheres present as hollow glass microspheres having a particle size distribution, d as , of from about 0.5 to about 2.7, wherein, d as ={(d a90 −d a10 )/d a50 } wherein d a10 is a particle size wherein 10% of the particles have a smaller particle size, d a50 is a median particle size wherein 50% of the particles have a smaller particle size, and d a90 is a particle size wherein 90% of the particle volume has a smaller particle size;
17) said proppant having microspheres present wherein said microspheres are uniformly present in said proppant or in a layered region of said proppant;
18) said optional ceramic whiskers have an average length of less than 5 microns;
19) said optional ceramic whisker have an average width of less than 0.35 micron;
20) said optional ceramic whiskers have a whisker length distribution, d as , of about 8 or less, wherein, d as ={(d a90 −d a10 )/d a50 } wherein d a10 is a whisker length wherein 10% of the whiskers have a smaller length, d a50 is a median whisker length wherein 50% of the whiskers have a smaller whisker length, and d a90 is a whisker length wherein 90% of the whiskers have a smaller whisker length;
21) said optional ceramic whiskers are present in an amount of from 5% to 60% by weight of said proppant;
22) said proppant has a combined clay amount and cristobalite amount of less than 20% by weight of proppant and said mullite whiskers are present in an amount of 60% or more by weight of said proppant;
23) said proppant has a uniform composition comprised of both crystalline and amorphous materials that extend from the inner portions of the proppant out through the surface; and/or,
24) said whiskers in said proppant are less euhedral and more anhedral.
15. The method of claim 14 , wherein one or more of said characteristics provide stress reducing properties on said proppant compared to the same proppant without said one or more characteristics.
16. The method of claim 14 , wherein said proppant comprises at least one layered shell encapsulating a hollow spherical template.
17. The method of claim 14 , wherein said proppant comprises at least one layered shell encapsulating a hollow spherical template, and said microspheres are present in said at least layered shell.
18. The proppant of claim 12 , wherein said whiskers are silicate mineral whiskers.