This disclosure provides casings and materials for the thermal management and protection of an electrochemical cell. The casing may also comprise a composite polymeric material for electrochemical cell thermal management, the composite polymeric material comprising a crosslinked polyether polyol phase change material configured to be in physical contact with at least a portion of an electrochemical cell.
1. A method for making a casing for the thermal management of an electrochemical cell, the method comprising:
combining one or more branching or crosslinking agents and a polyether polyol,
wherein the branching or crosslinking agent changes a length of a chain of the polyether polyol and forms a composite crosslinked polyether polyol phase change material; and
wherein the crosslinked polyether polyol phase change material: comprises crosslinks between two or more polymer side chains, the crosslinks having been formed by a dianhydrides or diisocyanate and polyether polyol in a ratio between approximately 0.5:1 and 1.5:1; and
forming the composite crosslinked polyether polyol phase change material into a casing having an inner surface configured to surround at least apportion of an electrochemical cell,
wherein the crosslinked polyether polyol phase change material has a transition temperature of between 25° C. and 140° C. and a latent heat of greater than 2 Joules per gram.
2. The method of claim 1 , wherein the polyether polyol comprises polyethylene glycol.
3. The method of claim 1 , wherein the branching or crosslinking agent comprises a branched crosslinking agent or chain extending agent.
4. A composite polymeric material for electrochemical cell thermal management, the composite polymeric material comprising:
a crosslinked polyether polyol phase change material configured to be in physical contact with at least a portion of an electrochemical cell,
wherein the crosslinked polyether polyol phase change material:
comprises crosslinks between two or more polymer chains, the crosslinks having been formed by a dianhydrides or a diisocyanate and a polyether polyol in a ratio between approximately 0.5:1 and 1.5:1; and
has a transition temperature of between 25° C. and 140° C. and a latent heat of greater than 2 Joules per gram.
5. The composite polymeric material of claim 4 , wherein the polyol comprises a branched polyol.
6. The composite polymeric material of claim 4 , wherein the material is machinable.
7. The composite polymeric material of claim 4 , wherein the material is moldable.
8. The composite polymeric material of claim 4 , wherein the material is a solid-solid phase change material.
9. The composite polymeric material of claim 4 , wherein the material is fire retardant.
10. The composite polymeric material of claim 4 , further comprising a thermal conductivity additive.
11. The composite polymeric material of claim 10 , wherein the material has a thermal conductivity of greater than 1.5 times the thermal conductivity of the crosslinked polyether polyol alone.
12. The method of claim 1 , wherein the polyol and the crosslinking agent or branching agent are reacted using a catalyst.
13. The composite polymer material of claim 4 , further comprising one or more of:
a water scavenger additive,
an antioxidant additive, or
a fire-retardant additive.
14. A casing for electrochemical cell thermal management, the casing comprising:
a substantially homogeneous crosslinked polyether polyol phase change material
wherein the crosslinked polyether polyol phase change material comprises crosslinks between two or more polymer chains, the crosslinks having been formed by a dianhydrides or a diisocyanate and a polyether polyol in a ratio between approximately 0.5:1 and 1.5:1; and has a transition temperature of between 25° C. and 140° C. and a latent heat of greater than 2 Joules per gram, and one or more receptacles configured to receive one or more electrochemical cells.
15. The casing of claim 14 , wherein the casing, when used in conjunction with one or more electrochemical cells during a plurality of charge and discharge cycles of the one or more electrochemical cells, extends the discharge capacity life of the one or more electrochemical cells as compared to the original discharge capacity life of the one or more electrochemical cells.
16. The casing of claim 14 , wherein an electrochemical cell, when retained within the casing, is capable of charging faster than a similar electrochemical cell that is not retained in the casing.
17. A casing for one or more electrochemical cells, the casing comprising:
a unitary structure comprised of a substantially homogeneous crosslinked polyether polyol phase change material, the unitary structure having one or more openings configured to retain the one or more electrochemical cells in thermal contact with the crosslinked polyether polyol phase change material,
wherein the crosslinked polyether polyol phase change material comprises crosslinks between two or more polymer chains, the crosslinks having been formed by a dianhydrides or a diisocyanate and a polyether polyol in a ratio between approximately 0.5:1 and 1.5:1; and has a transition temperature of between 25° C. and 140° C. and a latent heat of greater than 2 Joules per gram.
18. The composite polymeric material of claim 4 , wherein the polyether polyol is a copolymer.
19. The composite polymeric material of claim 4 , wherein the polyether polyol is a block copolymer.