Peel and stick roofing membranes with cured pressure-sensitive adhesives
View Patent ↗A membrane composite comprising a polymeric membrane panel, an adhesive layer, and a release member, where the adhesive layer is a pressure-sensitive adhesive that is at least partially cured, and where the adhesive layer has a thickness of at least 102 μm.
1. A process for forming a roofing membrane composite, the process comprising:
(a) heating a melt-extrudable, UV-curable pressure-sensitive adhesive to allow the adhesive to flow, where the adhesive consists of a polyacrylate elastomer and, optionally, one or more of photoinitiators, solvents, plasticizers, and resins selected from the group consisting of natural resins and hydrocarbon resins;
(b) applying the adhesive to a planar surface of a thermoplastic or cured rubber roofing membrane panel for providing a weatherproof polymeric barrier to a building structure, to thereby form a coating layer of adhesive having a thickness of at least 152 μm, where the roofing membrane panel has a thickness of from about 500 μm to about 3 mm;
(c) subjecting the coating layer of the adhesive to UV radiation to thereby effect crosslinking of the adhesive to form a cross-linked infinite polymer network;
(d) applying a release member to the adhesive coating layer to form a roofing member composite; and
(e) winding the composite.
2. The process of claim 1 , where said step of heating heats the adhesive to a temperature of from about 120 to about 160° C.
3. The process of claim 1 , where said step of subjecting the coating to UV radiation includes subjecting the adhesive to a UV dosage of from about 50 to about 230 millijoules/cm 2 .
4. The process of claim 1 , where said step of subjecting the coating to UV radiation includes subjecting the adhesive to at least 150 milliWatts/cm 2 of UV energy.
5. The process of claim 1 , where said step of subjecting the coating to UV radiation includes subjecting the adhesive to at least 200 milliWatts/cm 2 of UV energy.
6. The process of claim 1 , where the adhesive includes one or more units deriving from butyl acrylate or 2-ethylhexyl acrylate.
7. The process of claim 1 , where the adhesive has a Tg of less than 0° C.
8. The process of claim 1 , where the roofing membrane panel has a width of from about 1 to about 20 meters.