Method of manufacturing non-aqueous electrolyte secondary battery
A method of manufacturing a non-aqueous electrolyte secondary battery proposed herein includes a first binder supplying step ( 101 ), an active material supplying step ( 102 ), a second binder supplying step ( 103 ), and a pressing step ( 105 ). The first binder supplying step ( 101 ) is a step of applying a binder solution ( 122 ) to a current collector foil ( 121 ). The active material supplying step ( 102 ) is a step of supplying active material particles ( 123 ) onto the current collector foil ( 121 ) coated with the binder solution ( 122 ). The second binder supplying step ( 103 ) is a step of supplying the binder solution ( 122 ) onto the active material particles ( 123 ). The pressing step ( 105 ) is a step of pressing a layer of the active material particles ( 123 ) on the current collector foil ( 121 ).
1. A method of manufacturing a non-aqueous electrolyte secondary battery, comprising:
a first binder supplying step of applying a binder solution to a current collector foil;
an active material supplying step of supplying active material particles onto the current collector foil to which the binder solution has been applied;
a second binder supplying step of supplying a binder solution onto the active material particles; and
a pressing step of pressing a layer of the active material particles on the current collector foil.
2. The method according to claim 1 , wherein, in the first binder supplying step, the binder solution is supplied onto a surface of the current collector foil by gravure printing or ink-jet printing.
3. The method according to claim 1 , wherein the binder solution is an aqueous solution.
4. The method according to claim 1 , wherein a binder contained in the binder solution is an SBR.
5. The method according to claim 1 , wherein the current collector foil is a copper foil, and the active material particles are graphite particles.
6. The method according to claim 5 , wherein the graphite particles comprise spheroidal graphite.
7. The method according to claim 1 , further comprising, after the second binder supplying step and before the pressing step, a drying step of drying the current collector foil.
8. The method according to claim 7 , wherein the drying step comprises applying infrared rays to the current collector foil to which the binder solution and the active material particles have been supplied.
9. An electrode sheet comprising:
a current collector foil; and
a layer disposed on the current collector foil and comprising styrene-butadiene copolymer and active material particles only, the active material particles bonded to each other and to the current collector foil by the styrene-butadiene copolymer, and
wherein the layer includes a ⅓ thickness region from the current collector foil and a middle ⅓ thickness region, and the ⅓ thickness region from the current collector foil contains the binder in an amount at least 20% by volume greater than the middle ⅓ thickness region.
10. The electrode sheet according to claim 9 , wherein the layer further includes a ⅓ thickness region from a surface of the layer, and the ⅓ thickness region from the surface contains the binder in an amount at least 20% by volume greater than the middle ⅓ thickness region of the layer.