Antimicrobial polymer concentrates and compounds
Migratory assisting agents are used to improve antimicrobial efficacy of antimicrobial masterbatches, the polymer compounds these antimicrobial masterbatches are let down into, and the articles made therefrom. The migratory assisting agents function by carrying the antimicrobial agents while the migratory assisting agent transfers or “migrates” to the surface of a polymer compound or article formed from the polymer compound. As a result, antimicrobial agents are brought to the surface where there is exposure to bacterial contamination.
1. An antimicrobial masterbatch for thermoplastic compounds, comprising:
(a) a polymer carrier
(b) antimicrobial agent of a combination of silver-magnesium-aluminum phosphate complex and zinc pyrithione,
(c) from one to three weight percent of the masterbatch of a migratory assisting agent comprising a stearate, and
(d) optionally other additives.
2. The masterbatch of claim 1 , wherein the migratory assisting agent having anti-static properties comprises a glycerol mono stearate.
3. The masterbatch of claim 1 , wherein the migratory assisting agent will carry at least some of the antimicrobial agent to a surface of an article formed from the masterbatch.
4. The masterbatch of claim 1 , wherein the polymer carrier is selected from the group consisting of polyolefins, polyamides, polyesters, poly (meth)acrylates, polycarbonates, poly(vinyl halides), polyvinyl alcohols, polynitriles, polyacetals, polyimides, polyarylketones, polyetherketones, polyhydroxyalkanoates, polycaprolactones, polystyrenes, polyurethanes, polysulfones, polyphenylene oxides, polyphenylene sulfides, polyacetates, liquid crystal polymers, fluoropolymers, ionomeric polymers, thermoplastic elastomers, and copolymers of any of them and combinations of any two or more of them.
5. The masterbatch of claim 1 , wherein other additives are selected from the group consisting of anti-blocking agents; adhesion promoters; fungicides; mildewcides; anti-fogging agents; bonding, blowing and foaming agents; dispersants; fillers and extenders; fire and flame retardants and smoke suppressants; impact modifiers; initiators; lubricants; micas; pigments, colorants and dyes; plasticizers; processing aids; other slip or release agents; other anti-static agents; silanes, titanates and zirconates; stabilizers; stearates; ultraviolet light absorbers; viscosity regulators; waxes; and combinations of them.
6. An antimicrobial compound comprising the masterbatch of claim 1 and a base polymer resin.
7. The antimicrobial compound of claim 6 , wherein the base polymer resin is selected from the group consisting of polyolefins, polyamides, polyesters, poly (meth)acrylates, polycarbonates, poly(vinyl halides), polyvinyl alcohols, polynitriles, polyacetals, polyimides, polyarylketones, polyetherketones, polyhydroxyalkanoates, polycaprolactones, polystyrenes, polyurethanes, polysulfones, polyphenylene oxides, polyphenylene sulfides, polyacetates, liquid crystal polymers, fluoropolymers, ionomeric polymers, thermoplastic elastomers, and copolymers of any of them and combinations of any two or more of them.
8. The antimicrobial compound of claim 6 , wherein the compound when extruded into an article has an improved gram (−) log and gram (+) log according to the JIS Z 2801 test method, compared to the compound without the migratory assisting agent.
9. The antimicrobial compound of claim 6 , further comprising additives selected from the group consisting of anti-blocking agents; adhesion promoters; fungicides; mildewcides; anti-fogging agents; bonding, blowing and foaming agents; dispersants; fillers and extenders; fire and flame retardants and smoke suppressants; impact modifiers; initiators; lubricants; micas; pigments, colorants and dyes; plasticizers; processing aids; other slip or release agents; other anti-static agents; silanes, titanates and zirconates; stabilizers; stearates; ultraviolet light absorbers; viscosity regulators; waxes; and combinations of them.
10. The antimicrobial compound of claim 6 , wherein the amount of masterbatch let down into base resin ranges from 1% to 10% of the weight percent of the compound.
11. The antimicrobial compound of claim 6 , in the shape of a molded plastic article, an extruded plastic article, a calendered plastic article, a thermoformed plastic article, or a 3D printed plastic article.
12. A molded article made from the antimicrobial compound of claim 6 .
13. An extruded article made from the antimicrobial compound of claim 6 .
14. A calendered article made from antimicrobial compound of claim 6 .
15. A thermoformed article made from the antimicrobial compound of claim 6 .
16. The masterbatch of claim 2 , wherein the migratory assisting agent will carry at least some of the antimicrobial agent to a surface of an article formed from the masterbatch.
17. An antimicrobial compound comprising the masterbatch of claim 2 and a base polymer resin.
18. The antimicrobial compound of claim 17 , wherein the compound when extruded into an article has an improved gram (−) log and gram (+) log according to the JIS Z 2801 test method, compared to the compound without the migratory assisting agent.
19. The antimicrobial compound of claim 18 , wherein the amount of masterbatch let down into base resin ranges from 1% to 10% of the weight percent of the compound.