Continuous casting method
In a continuous casting method for casting an aluminum-deoxidized molten stainless steel 1 by using a continuous casting apparatus 100 in which a long nozzle 3 extending into a tundish 101 is provided at a ladle 2 , the molten stainless steel 1 is poured through the long nozzle 3 into the tundish 101 , while immersing a spout 3 a into the poured molten stainless steel 1 , and the molten stainless steel 1 in the tundish 101 is poured into a casting mold 105 . A TD powder 5 is sprayed so that the powder covers the surface of the molten stainless steel 1 in the tundish 101 , a nitrogen gas is supplied around the molten stainless steel 1 , and a calcium-containing material is added to the molten stainless steel 1 in the tundish 101 . The surface of the molten stainless steel 1 after casting is ground.
1. A continuous casting method for casting a solid metal by pouring a molten metal, subjected to aluminum deoxidation in a ladle, into a tundish and continuously pouring the molten metal in the tundish into a casting mold, the continuous casting method including:
a long nozzle installation step for providing in the ladle a long nozzle extending into the tundish as a pouring nozzle for pouring the molten metal in the ladle into the tundish;
a casting step for pouring the molten metal into the tundish through the long nozzle, while immersing a spout of the long nozzle into the molten metal poured into the tundish, and pouring the molten metal in the tundish into the casting mold;
a spraying step for spraying a tundish powder so that the powder covers the surface of the molten metal in the tundish;
a seal gas supply step for supplying a nitrogen gas as a seal gas around the molten metal sprayed with the tundish powder;
a calcium-containing material addition step for adding a calcium-containing material to the molten metal retained in the tundish; and
a grinding step for grinding the surface of the cast solid metal.
2. The continuous casting method of claim 1 , wherein the molten metal includes titanium as a component.
3. The continuous casting method of claim 1 , wherein the calcium-containing material is a calcium-containing wire, and the calcium-containing wire is added to the molten metal sprayed with the tundish powder.
4. The continuous casting method of claim 1 , wherein before the tundish powder is sprayed, argon gas is supplied as a seal gas around the molten metal in the tundish.