Thermosetting powder coating compositions comprising methyl-substituted benzoyl peroxide
View Patent ↗The invention relates to thermosetting powder coating compositions comprising an unsaturated resin comprising ethylenic unsaturations and a thermal radical initiator comprising a first thermal radical initiator, wherein the first thermal radical initiator is a methyl-substituted benzoyl peroxide abbreviated herein as MBPO. The invention further relates to a process for making said thermosetting powder coating composition and processes for coating an article with said thermosetting powder coating composition. The invention further relates to a cured thermosetting powder coating composition derived upon curing of the thermosetting powder coating composition of the invention. The invention further relates to an article having coated thereon said thermosetting powder coating composition as well as to an article having coated and cured thereon said thermosetting powder coating composition. The invention further relates to the use of said thermosetting powder coating composition, to the use of an article having coated thereon said thermosetting powder coating composition and to the use of an article having coated and cured thereon said thermosetting powder coating composition. The invention further relates to cured thermosetting powder coating compositions derived upon curing of the thermosetting powder coating compositions comprising an unsaturated resin comprising ethylenic unsaturations and a first thermal radical initiator, said first thermal radical initiator being methyl-substituted benzoyl peroxide, abbreviated herein as MBPO. The invention further relates to the use of MBPO for thermosetting powder coating compositions and especially wherein the thermosetting powder coating compositions are heat-curable at low temperatures on heat-sensitive articles.
1. A thermosetting powder coating composition comprising:
(A) an unsaturated resin comprising ethylenic unsaturations (UR), that is an unsaturated polymer having i) and ii):
i) a theoretical number average molecular weight (Mn) of at least 200 and at most 20000 Da, and
ii) ethylenic unsaturations which are cis- or trans-configured reactive carbon-carbon double bond unsaturations and do not include aromatic unsaturations, carbon-carbon triple bonds, carbon-heteroatom unsaturations; wherein
the UR is selected from the group consisting of polyester resins, acrylic resins, polyurethanes, epoxy resins, polyamides, polyesteramides, polycarbonates, polyureas and mixtures thereof; and
(B) a thermal radical initiator comprising a first thermal radical initiator, wherein
the first thermal radical initiator is a methyl-substituted benzoyl peroxide.
2. The thermosetting powder coating composition according to claim 1 , wherein the first thermal radical initiator is selected from the group consisting of bis-(2-methylbenzoyl)-peroxide, bis-(3-methylbenzoyl)-peroxide, bis-(4-methylbenzoyl)-peroxide, (2-methylbenzoyl, 3-methylbenzoyl)-peroxide, (2-methylbenzoyl, 4-methylbenzoyl)-peroxide, (3-methylbenzoyl, 4-methylbenzoyl)-peroxide and mixtures thereof.
3. The thermosetting powder coating composition according to claim 1 , wherein the first thermal radical initiator is selected from the group consisting of bis-(4-methylbenzoyl)-peroxide, (2-methylbenzoyl, 4-methylbenzoyl)-peroxide, (3-methylbenzoyl, 4-methylbenzoyl)-peroxide and mixtures thereof.
4. The thermosetting powder coating composition according to claim 1 , wherein the first thermal radical initiator is bis-(4-methylbenzoyl)-peroxide.
5. The thermosetting powder coating composition according to claim 1 , wherein the amount of thermal radical initiator is at least 0.1 and at most 20 pph.
6. The thermosetting powder coating composition according to claim 1 , wherein the amount of thermal radical initiator is at least 0.1 and at most 15.2 pph.
7. The thermosetting powder coating composition according to claim 1 , wherein the amount of thermal radical initiator is at least 2 and at most 9 pph.
8. The thermosetting powder coating composition according to claim 1 , wherein the thermal radical initiator comprises the first thermal radical initiator in an amount of at least 10% w/w based on the total amount of the thermal radical initiator.
9. The thermosetting powder coating composition according to claim 1 , wherein the thermal radical initiator comprises the first thermal radical initiator in an amount of at least 50% w/w based on the total amount of the thermal radical initiator.
10. The thermosetting powder coating composition according to claim 1 , wherein the thermal radical initiator comprises the first thermal radical initiator in an amount of at least 90% w/w based on the total amount of the thermal radical initiator.
11. The thermosetting powder coating composition according to claim 1 , wherein the UR is selected from the group consisting of polyester resins, polyurethanes, polyamides, polyesteramides, polyureas and mixtures thereof.
12. The thermosetting powder coating composition according to claim 1 , wherein the ethylenic unsaturations of the UR are di-acid ethylenic unsaturations.
13. The thermosetting powder coating composition according to claim 1 , wherein the UR is an unsaturated polyester resin comprising ethylenic unsaturations.
14. The thermosetting powder coating composition according to claim 1 , wherein the UR is an unsaturated polyester resin comprising di-acid ethylenic unsaturations.
15. The thermosetting powder coating composition according to claim 1 , wherein the UR is an unsaturated polyester resin comprising 2-butenedioic acid ethylenic unsaturations.
16. The thermosetting powder coating composition according to claim 1 , further comprising: (C) a curing agent and/or (D) an accelerator and/or (E) a co-accelerator and/or (F) an inhibitor.
17. The thermosetting powder coating composition according to claim 16 , wherein the amount of inhibitor is at least 0.025 and at most 0.20 pph.
18. The thermosetting powder coating composition according to claim 16 , wherein the curing agent is a vinyl functionalized urethane resin selected from the group consisting of vinyl ether functionalized urethane resin, vinyl ester functionalized urethane resin and mixtures thereof.
19. The thermosetting powder coating composition according to claim 16 , wherein the curing agent is a vinyl ether functionalized urethane resin.
20. The thermosetting powder coating composition according to claim 1 , wherein
the UR is an unsaturated polyester resin comprising di-acid ethylenic unsaturations, and
the first thermal radical initiator is bis-(4-methylbenzoyl)-peroxide and
the amount of thermal radical initiator is at least 0.1 and at most 15.2 pph, and
the thermal radical initiator comprises the first thermal radical initiator in an amount of at least 50% w/w based on the total amount of the thermal radical initiator.
21. The thermosetting powder coating composition according to claim 20 , further comprising:
(C) a curing agent, said curing agent being a vinyl ether functionalized urethane resin, and
(D) an inhibitor.
22. A process for making a thermosetting powder coating composition as defined in claim 1 , comprising the steps of:
(a) mixing the components of the thermosetting powder coating composition to obtain a premix;
(b) heating the premix in an extruder, to obtain an extrudate;
(c) cooling down the extrudate to obtain a solidified extrudate; and
(d) grinding the solidified extrudate into smaller particles to obtain the thermosetting powder coating composition.
23. A cured thermosetting powder coating composition derived upon curing of a thermosetting powder coating composition as defined in claim 1 .
24. An article having coated thereon a thermosetting powder coating composition as defined in claim 1 .
25. An article having coated and cured thereon a thermosetting powder coating composition as defined in claim 1 .
26. A process for making a coated article comprising the steps of:
(a) applying a thermosetting powder coating composition as defined in claim 1 to an article; and
(b) heating and/or radiating the thermosetting powder coating composition for enough time and at a suitable temperature to cure the thermosetting powder coating composition and thereby obtain the coated article.
27. The thermosetting powder coating composition according to claim 1 , wherein the composition is a powder coating composition is applied as a powder coating in an application selected from the group consisting of heat-sensitive articles, non-heat-sensitive articles, 3D-printing applications, automotive applications, marine applications, aerospace applications, medical applications, defense applications, sports/recreational applications, architectural applications, bottling applications, household applications, machinery applications, can applications, coil applications, energy applications, textile applications and electrical applications.
28. The thermosetting powder coating composition according to claim 3 , wherein the amount of thermal radical initiator is at least 0.1 and at most 20 pph.
29. The thermosetting powder coating composition according to claim 3 , wherein the amount of thermal radical initiator is at least 0.1 and at most 15.2 pph.
30. The thermosetting powder coating composition according to claim 3 , wherein the amount of thermal radical initiator is at least 2 and at most 9 pph.
31. The thermosetting powder coating composition according to claim 4 , wherein the amount of thermal radical initiator is at least 0.1 and at most 20 pph.
32. The thermosetting powder coating composition according to claim 4 , wherein the amount of thermal radical initiator is at least 0.1 and at most 15.2 pph.
33. The thermosetting powder coating composition according to claim 4 , wherein the amount of thermal radical initiator is at least 2 and at most 9 pph.
34. The thermosetting powder coating composition according to claim 3 , wherein the thermal radical initiator comprises the first thermal radical initiator in an amount of at least 90% w/w based on the total amount of the thermal radical initiator.
35. The thermosetting powder coating composition according to claim 4 , wherein the thermal radical initiator comprises the first thermal radical initiator in an amount of at least 90% w/w based on the total amount of the thermal radical initiator.
36. The thermosetting powder coating composition according to claim 3 , further comprising: (C) a curing agent and/or (D) an accelerator and/or (E) a co-accelerator and/or (F) an inhibitor.
37. The thermosetting powder coating composition according to claim 4 , further comprising: (C) a curing agent and/or (D) an accelerator and/or (E) a co-accelerator and/or (F) an inhibitor.
38. The thermosetting powder coating composition according to claim 36 , wherein the amount of inhibitor is at least 0.025 and at most 0.20 pph.
39. The thermosetting powder coating composition according to claim 37 , wherein the amount of inhibitor is at least 0.025 and at most 0.20 pph.
40. A cured thermosetting powder coating composition derived upon curing of a thermosetting powder coating composition as defined in claim 3 .
41. A cured thermosetting powder coating composition derived upon curing of a thermosetting powder coating composition as defined in claim 4 .
42. A cured thermosetting powder coating composition derived upon curing of a thermosetting powder coating composition as defined in claim 20 .
43. A cured thermosetting powder coating composition derived upon curing of a thermosetting powder coating composition as defined in claim 21 .
44. A cured thermosetting powder coating composition derived upon curing of a thermosetting powder coating composition as defined in claim 20 , wherein the amount of inhibitor is at least 0.025 and at most 0.20 pph.
45. A cured thermosetting powder coating composition derived upon curing of a thermosetting powder coating composition as defined in claim 21 , wherein the amount of inhibitor is at least 0.025 and at most 0.20 pph.
46. The thermosetting powder coating composition according to claim 20 , wherein the composition is applied in an application selected from the group consisting of heat-sensitive articles, non-heat-sensitive articles, 3D-printing applications, automotive applications, marine applications, aerospace applications, medical applications, defense applications, sports/recreational applications, architectural applications, bottling applications, household applications, machinery applications, can applications, coil applications, energy applications, textile applications and electrical applications.